1) corrosion depth
蚀损深度
1.
For corroded region of materials, microstructure, element distribution and corrosion depth were observed and determined by electro-probe microanalysis.
结果表明:材料被侵蚀后结构发生变化,可大致分为渣带、渗透带和未变带;随材料中TiN含量的增加,材料的蚀损深度减小,渣带和渗透带变窄,抗渣侵蚀性能增强;TiN/O′ Sialon的抗渣侵蚀性能优于O′ Sialon和ZrO2/O′ Sialon;随侵蚀温度升高、侵蚀时间延长和渣中FeO含量增大,材料的蚀损深度增加,其中侵蚀温度的影响最为显著。
2) erosion
蚀损
1.
Ideas to upgrade its performance and development direction are also put forward on the discussion of erosion theory.
本文叙述了包钢新型耐火材料股份有限公司现行生产镁碳砖的工艺技术和在 90t精炼钢包渣线使用的情况 ,通过对蚀损机理的探讨 ,提出性能改进观点以及发展方向。
3) corrosion
蚀损
1.
Experiment of influence of mould powder on corrosion resistance of dipping brick was done.
为了阐明浸入式水口在保护渣线周围使用的 Zr O2 —石墨质耐火材料的蚀损机理 ,进行了多种保护渣在感应电炉内的侵蚀试验。
2.
To understand the corroding mechanism of ZrO_2-C slag line of nozzle in mold fluxes,the corrosion experiments were carried out.
为了阐明水口渣线用 ZrO_2-C 质的耐火材料与保护渣的蚀损机理,进行了不同含氟保护渣侵蚀试验。
3.
To understand the corroding mechanism of ZrO_2-C slag line of SEN in mold fluxes,the corrosion experiments were carried out.
为了阐明浸入式水口渣线用 ZrO_2-C 质的耐火材料与保护渣的蚀损机理,进行了不同含氟保护渣侵蚀试验。
4) pitting attack damage
点蚀损伤
1.
By the examination of metallographic microstructure and the hardness analysis of failure gear after used, the main reason that the pitting attack damage appears on the surface of gear was found.
通过对使用后失效齿轮的金相组织检验及硬度分析,找出齿轮表面产生点蚀损伤的主要原因,并提出了相应的改进措施。
5) Corrosion mechanism
蚀损机理
6) Corrosion damage
腐蚀损坏
1.
The causes of corrosion damage are elaborated based upon the properties of base materials and the impact of local environment on circulating cooling water towers,and the protective mea-sures are also put forward in the paper.
根据冷却水塔的基体材料特性和所处的环境影响,说明冷却水塔的腐蚀损坏,同时提出防护措施。