1) U monomer
PU-大单体
2) polyurethane elastomer
PU弹性体
1.
Using the natural graphite as packing materials,the heat-resistant polyurethane elastomers was prepared by the method of pre-polymerization.
热分解温度聚酯型PU弹性体提高了30℃,聚醚型提高了近40℃。
2.
ln this paper,polyurethane elastomer,spandex,spandex fiber and new trend in their local raw materials market were reviewed.
对聚氨酯(PU)弹性体氨纶、热塑性聚氨酯弹性体(TPU)及其上游一些原料国内市场最新动态作了介绍和浅析,指出国内氨纶需提高技术创新能力和国际竞争力;国内TPU产业应发展高端产品;并介绍PU弹性体最新技术进展和新的应用,提出了我国未来PU弹性体重点发展方向。
3.
In this paper, polyurethane elastomer, spandex fiber and n ew trend in their local raw materials market are reviewed.
市场分析表明PU弹性体快速发展推动了一些上游原料的发展,聚四氢呋喃(PTMEG)和N,N-二甲基甲酰胺(DMF)出现供过于求的趋势。
3) PU elastomer
PU弹性体
1.
Preparation of prepolymer for soft PU elastomer and its application;
软质PU弹性体用预聚体的制备及其应用
2.
A cast PU elastomer was prepared with polyester g lycol,toluene diisocyanate (TDI) and chain extender.
以聚酯二醇、甲苯二异氰酸酯 (TDI)和扩链剂为原料 ,制备浇注型PU弹性体 ,研究了预聚法和一步法、聚酯与聚醚、80 / 2 0 TDI和 2 ,4 TDI、聚酯二醇的种类及其相对分子质量、弹性体交联点相对分子质量和硬段质量分数对弹性体力学性能的影响。
3.
These formula will have wide applications in the study of the propertystructure relationship of PU elastomers and PU propellants, and the quality control of PU solid propellants.
这些公式在PU弹性体及PU推进剂结构与性能之间关系的研究和PU泡沫、弹性体、PU固体推进剂等制品的质量控制中,将有广泛的应用。
4) plutonium(Ⅳ)
Pu()
5) macromonomer
大单体
1.
The macromonomer possessed excellent photosensitivity,and a kind of novel transparent polymer material was synthesized through crosslinking of the macromonomer and curing by ultraviolet radiation.
以异氟尔酮-二异氰酸酯(IPDI)、聚乙二醇(PEG)、N-羟甲基丙烯酰胺等为主要原料,利用大单体合成技术,制备了两端由丙烯酰胺基团封端的聚氨酯大分子单体。
2.
Polystyrene-g-polydimethylsiloxane copolymers were prepared by using the methacryloxypropyl-polysiloxane(PDMS-MA) macromonomer technique.
以甲基丙烯酰氧丙基聚硅氧烷大单体(PDMS-MA)与苯乙烯共聚合,制备了聚苯乙烯聚硅氧烷梳状接枝共聚物(PSt-g-PDMS),采用傅里叶变换红外光谱(FTIR)表征了接枝共聚物的组成,研究了聚硅氧烷大单体的相对分子质量对共聚合活性的影响,并对接枝共聚物的热性能进行了表征。
3.
A hyperbranched macromonomer(3) was synthesized with maleic anhydride,diethanolamine,o-phthalic anhydride by step polymerization,take advantage of the different activities of functional groups.
以顺丁烯二酸酐、二乙醇胺、邻苯二甲酸酐等为原料,利用官能团活性的差异,通过逐步展开的方法合成了含有双键和端羟基的聚(酯-酰胺)型分子结构的超支化大单体(3)。
6) macromer
大单体
1.
Studies on Acrylamide-Dicyanodiamide Macromer and Its Copolymer with Styrene (Ⅰ) --The Synthesis and Characterization of Macromer and Its Copolymer;
丙烯酰胺-二氰二胺大单体及其与苯乙烯共聚物的研究(Ⅰ)——大单体及其共聚物的合成和表征
2.
Graft terpolymerization of polyoxyethylene macromer with acrylates;
聚环氧乙烷大单体与丙烯酸酯的三元接枝共聚
3.
The poly(methyl methacryate)macromer was copolymerized with butyl acrylate i n benzene to form the graft copolymer.
研究了聚甲基丙烯酸甲酯大单体与丙烯酸丁酯在苯中的共聚。
补充资料：reduction of Pu(IV)to Pu(III)
分子式：
CAS号：
性质：by U(IV)铀(IV)是一种钚(IV)的很好的还原剂，已广泛应用于后处理工业，特别是共去污循环。其反应式为 反应速率比亚铁还原钚(IV)稍慢，但反应完全。当铀(IV)用作还原剂时，需要加入支持还原剂破坏亚硝酸，以防止U4+被亚硝酸氧化。常用的支持还原剂是肼。为了保证钚还原完全，加入的铀(IV)量应使铀(IV)/钚(III)比值在3～8之间，还原剂中硝酸浓度为0.5～2mol/L，硝酸肼浓度为0.1～0.2mol/L。
CAS号：
性质：by U(IV)铀(IV)是一种钚(IV)的很好的还原剂，已广泛应用于后处理工业，特别是共去污循环。其反应式为 反应速率比亚铁还原钚(IV)稍慢，但反应完全。当铀(IV)用作还原剂时，需要加入支持还原剂破坏亚硝酸，以防止U4+被亚硝酸氧化。常用的支持还原剂是肼。为了保证钚还原完全，加入的铀(IV)量应使铀(IV)/钚(III)比值在3～8之间，还原剂中硝酸浓度为0.5～2mol/L，硝酸肼浓度为0.1～0.2mol/L。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条