1) polystyrene macromer
聚苯乙烯大单体
1.
Effect of polymerization conditions including charging weight ratio of polystyrene macromer,amount of initiator and temperature of copolymerization on grafting efficiency were studied.
研究了共聚合反应条件:聚苯乙烯大单体的投料质量分数,引发剂用量,反应温度对接枝效率的影响;PBA-g-PS可以作为ACR/PS体系的共混增容剂,研究共混物的组成,接枝物的用量,接枝物的组成对共混物物理机械性能的影响。
2.
Effect of polymerization conditions including charging mass fraction of polystyrene macromer,amount of initiator and temperature of copolymerization on grafting efficiency were studied.
采用聚苯乙烯大单体和丙烯酸辛酯进行自由基溶液共聚合反应,得到规整接枝共聚物。
2) PEO-macromonomer
聚氧乙烯大单体
1.
By means of measurement of FTIR and 13CNMR, it demonstrated that the synthesized microparticle is composed of chain units of acrylamide, PEO-macromonomer, acryloyloxyethyl trimethylammonium chloride, N,N′-methylenebis-acrylam.
FTIR谱和13 CNMR谱的测试结果证明所合成的微粒是由丙烯酰胺、聚氧乙烯大单体、丙烯酰氧基乙基三甲基氯化铵和N ,N′ 亚甲基双丙烯酰胺 4种链节所组成 ,而且各链节的比例与原料配比基本相
3) monodisperse polystyrene colloid
单分散聚苯乙烯胶体
补充资料：聚苯乙烯/聚乙烯共混物
分子式：
CAS号：
性质：由聚苯乙烯与聚乙烯系列为主组成的共混物，添加少量第三组分，如氢化丁苯嵌段共聚物或接枝共聚物等作增容剂，既有聚苯乙烯良好的成型加工性和刚性，又改善其脆性、应力开裂及耐油性，例如：80份聚苯乙烯与20份聚乙烯共混，加入10份氢化丁苯热塑性弹性体，冲击强度可达36.7kJ/m2，拉伸强度为20.8MPa，可通过机械共混或反应挤出共混制备，用于含油脂较多的食品包装容器，如乳制品包装等方面。
CAS号：
性质：由聚苯乙烯与聚乙烯系列为主组成的共混物，添加少量第三组分，如氢化丁苯嵌段共聚物或接枝共聚物等作增容剂，既有聚苯乙烯良好的成型加工性和刚性，又改善其脆性、应力开裂及耐油性，例如：80份聚苯乙烯与20份聚乙烯共混，加入10份氢化丁苯热塑性弹性体，冲击强度可达36.7kJ/m2，拉伸强度为20.8MPa，可通过机械共混或反应挤出共混制备，用于含油脂较多的食品包装容器，如乳制品包装等方面。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。