1) oxalic acid anodizing
草酸阳极氧化
2) oxalic anodizing
草酸阳极氧化
1.
High current density and voltage used in oxalic anodizing and hard anodizing process cause quantities of bath heat.
草酸阳极氧化、硬质阳极氧化处理工艺电流密度大、电压高、产热量大,必须采用压缩空气不断搅拌槽液,由此可能导致工件与挂具接触不良,引起工件烧伤和报废。
3) ~+Oxidation of oxalic acidpositive pole
~+草酸阳极氧化
4) oxalic acid
草酸
1.
Study on preparation of oxalic acid from peanut hulls;
用花生壳制取草酸的研究
2.
Growth kinetics and morphological structure of porous anodic aluminum oxide films formed in oxalic acid;
草酸中多孔阳极氧化铝膜生长动力学和形态结构研究(英文)
3.
Determination of glyoxalic acid and oxalic acid by high performance liquid chromatography;
乙醛酸和草酸的高效液相色谱分析
5) Oxalate
草酸
1.
Study on the Determining Conditions of Oxalate Content in Spinach with Coloration Method;
比色法测定菠菜中草酸含量的条件研究
2.
Catalytic Fluorimetric Determination of Trace Oxalate;
催化荧光法测定痕量草酸
3.
Consistency of oxalate record between Tianshan and Everest regions and its environmental significance.;
天山与珠峰冰芯草酸根的一致性及其环境意义
6) ethanedioic acid
草酸
参考词条
补充资料：草酸阳极氧化
分子式：
分子量：
CAS号：
性质：铝及其合金在草酸溶液中（溶液温度一般为15-18℃或32℃±+2℃），在直流电流（电压为110-120伏或40-60伏）的作用下，工件（阳极）上形成氧化膜层。膜层厚约为8-20微米，抗蚀能力和硬度与硫酸阳极氧化膜差不多。绝缘性能良好，在不含铜的纯铝及其合金上可以获得银白色、黄铜色、黄褐色的装饰性膜层。
分子量：
CAS号：
性质：铝及其合金在草酸溶液中（溶液温度一般为15-18℃或32℃±+2℃），在直流电流（电压为110-120伏或40-60伏）的作用下，工件（阳极）上形成氧化膜层。膜层厚约为8-20微米，抗蚀能力和硬度与硫酸阳极氧化膜差不多。绝缘性能良好，在不含铜的纯铝及其合金上可以获得银白色、黄铜色、黄褐色的装饰性膜层。