1) re-ageing
过时效处理
1.
The experimental results show that the electrical conductivity of the over-aged alloy in 120℃×3h+180℃×8h temper decreased with increase of re-solution temperature after re-solution in the range of 440℃～490℃×1h and 120℃×24h re-ageing, but the strength lowered correspondingly.
采用拉伸试验、电导率测试及透射电镜观察等方法 ,研究了重固溶温度和过时效处理时间对70 5 5铝合金组织与性能的影响。
2) "out-of-date"
“过时”
3) outdated
过时
1.
At the same time, however, there are some people who argue that it is outdated about peasant s image and it isn t useful to exist.
但与此同时，也出现了一些声音，认为表现农民形象的绘画已经过时、没有存在的意义了。
4) overaging
过时效
1.
A Study on Temper Embrittlement Overaging Phenomenon of Alloy Steel 2.25Cr-1Mo;
2.25Cr-1Mo合金钢回火脆化过时效现象的研究
2.
The recrystallization,austenization and overaging of cold rolled strip during continuous annealing were investigated by optical microscopy and scanning electron microscopy.
采用光学显微镜与扫描电镜观察分析了实验钢冷轧组织在连续退火过程中的再结晶与相变规律,研究了过时效回火对双相钢显微组织的影响。
5) over ageing
过时效
1.
The effect of over ageing (OA) and temper rolling on the mechanical properties of cold rolled low carbon SiMn dual phase steel sheets has been studied.
以低碳Si Mn系冷轧双相钢为研究对象,探讨了过时效和平整工艺对双相钢板力学性能的影响。
2.
Effect of over ageing on the mechanical properties and microstructure of Si Mn dual phase steel sheets was studied.
研究过时效温度和时间对低碳Si Mn冷轧双相钢的力学性能和组织的影响 ,结果发现 ,过时效温度对双相钢力学性能影响很大。
6) over-aged
过时效态
1.
Fatigue behavior of over-aged 2A12 alloys in a vacuum environment;
真空环境下过时效态2A12合金的疲劳行为
参考词条
补充资料：过时效
overaging：与获得最佳力学性能（强度和硬度）的时效处理条件相比，过时效是指在温度过高或时间过长条件下发生的时效现象。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。