1) TiO_2/SiO_2 composite
TiO2/SiO2混合氧化物
1.
The TiO_2/SiO_2 composite with high specific surface area was prepared by a two step hydrolysis method.
采用两步水解法制备了高比表面积的TiO2/SiO2混合氧化物,利用TGA和低温N2的吸附对粉体进行了表征。
2) TiO_2-SiO_2 mixed oxides
TiO2-SiO2混合氧化物
1.
Adsorptive and photocatalytic degradation efficiency of TiO_2-SiO_2 mixed oxides for color organics in paper-making waste water are studied.
研究了TiO2-SiO2混合氧化物对纸业废水中有色有机物的吸附与光催化降解效率。
3) SiO2-TiO2 mixed oxide
SiO2-TiO2复合氧化物
1.
SiO2-TiO2 mixed oxide was prepared by the homogeneous precipitation method using tetraethoxysilane and tetrabutyl titanate as precursors,and the structure of the products was characterized by X-ray diffraction(XRD).
以正硅酸乙酯和钛酸正丁酯作前体,通过均匀沉淀法制备了SiO2-TiO2复合氧化物,并采用X射线粉末衍射(XRD)对复合氧化物进行了表征。
4) Fe2O3-SiO2 mixed oxide
Fe2O3-SiO2混合氧化物
1.
The precursors of Fe2O3-SiO2 mixed oxides prepared via co-precipitation method with Fe(NO3)3·9H2O and Na2SiO3 as starting materials were modified by heating in water bath or microwave hydrothermal treatment respectively.
对共沉淀法得到的Fe2O3-SiO2混合氧化物前驱物进行水浴及微波水热改性处理,经负载S2O82-并高温焙烧处理后得S2O82-/Fe2O3-SiO2固体酸催化剂,用乙酸/丁醇酯化催化反应评估该催化剂的催化活性。
5) Fe_2O_3-SiO_2 composite oxide
Fe2O3-SiO2复合氧化物
6) CeO_2-SiO_2 mixed oxide
CeO2-SiO2复合氧化物
补充资料：CaO-TiO2-SiO2 ceramics
分子式：
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条