1) One-Step Melt Blending in One-Pot
一步熔融共混法
1.
High impact polystyrene (HIPS) composites containing both thane-1,2-bis(pentabromophenyl) (SAYTEX 8010)-antimony (Sb 2O 3) and Montmorillonite (MMT)- Hexadecyl trimethyl ammonium bromide (C16BrN, combination with MMT at different modification ratio) fire retarding system packages were prepared by One-Step Melt Blending in One-Pot.
运用"一步熔融共混法"制备了同时包含十溴二苯乙烷(SAYTEX8010)-氧化锑(Sb2O3)和蒙脱土(MMT)-十六烷基三甲基溴化铵(C16BrN)(不同重量比率)阻燃体系的系列高抗冲聚苯乙烯(HIPS)复合材料,通过X射线衍射(XRD)、透射电镜(TEM)、UL-94垂直燃烧测试和锥形量热计等测试手段对其结构形貌和燃烧性能进行了表征,探讨了两种阻燃体系间的协效性及蒙脱土改性比率对协效度的影响。
2) melt blending
熔融共混
1.
PP/nano-Ti-alloy composites were prepared by melt blending of PP with nano-Ti-alloy.
将纳米钛合金与聚丙烯(PP)经熔融共混制得PP/纳米钛合金复合材料,研究了PP及其复合材料在大气暴露条件下的耐候性,利用傅立叶变换红外光谱仪分析了老化前后PP及其复合材料的化学结构。
2.
Poly(propylene carbonate)/polystyrene(PPC/PS) composites were prepared by melt blending followed by hot compression molding.
利用熔融共混的方法制备了聚丙撑碳酸酯/聚苯乙烯(PPC/PS)复合材料,并通过万能试验机、差示扫描量热分析仪(DSC)、热重分析仪(TG)以及扫描电子显微镜(SEM)分别研究了复合材料的力学性能、热性能及微观形态。
3.
The POE/PP composite was made through melt blending.
用熔融共混法制得了聚烯烃类弹性体(POE)/PP共混体系,研究了不同橡塑比对体系力学性能的影响;考察了不同填料(CaCO3,滑石粉,炭黑)对POE/PP复合材料性能的影响。
3) melt blend
熔融共混
1.
A material for oil adsorption composites was prepared by melt blend method with EPDM as the matrix, the cast-off of mineral extraction(mineral powder)as the filler.
以三元乙丙橡胶(EPDM)作为基体,矿物提取后的废弃物(矿粉)为填料,利用熔融共混的方法,制备出一种新型吸油复合材料,这类材料可以直接漂浮于含油废水表面使用。
2.
The method of preparation by melt blend is compared with intercalation polymerization.
综述了尼龙6/蒙脱土纳米复合材料的制备、结构、性能及应用,比较了插层聚合法和熔融共混法2种制备工艺,介绍了蒙脱土来源、尼龙品种对复合材料结构及性能的影响。
3.
PPS/PEEK melt blend prepared by melt-blending is introduced,and the influence of a dif- ferent content of PEEK and a different size of PEEK particales on the crystallization behavior of PPS in the PPS/PEEK blend is investigated by DSC.
采用熔融共混法制备结晶/结晶共混体系PPS/PEEK,并用差示扫描量热法研究了不同PEEK含量和不同PEEK粒径对PPS/PEEK共混物中PPS组分结晶行为的影响。
4) melt-blending
熔融共混
1.
A composite material of SiO2-g-PS nano-microsphere and polypropylene(PP)was prepared by the melt-blending process and the mechanical performance was investiga.
通过熔融共混工艺制备聚丙烯(PP)基复合材料,并对其力学性能进行了分析,结果表明,当SiO2-g-PS填充量较低[4%～6%(质量)]时,SiO2-g-PS/PP复合材料的冲击强度和拉伸强度明显提高,并对PP的结晶有明显的异相成核作用。
2.
Polypropylene/nano-SiO-2 composites were prepared by melt-blending process.
通过熔融共混法制备了SiO2 分散很好的聚丙烯 /纳米SiO2 复合材料。
3.
We used the method of Solution-Compound and Melt-Blending to prepare the PP/ATPcomposite.
本文以PP为聚合物基体,以天然ATP为无机组分,通过溶液复合、熔融共混两种方法制备了PP/ATP纳米复合材料。
5) Melting Blend
熔融共混
1.
Methods\ PP/SiO\-2 nanocomposites are produced by melting blend process and then the best dosage of silicane KH 560 is discussed by analyzing its mechanical behaviors and SEM photo graghs.
方法 首先用熔融共混法制备 PP/Si O2 纳米粒子复合材料 ,再通过分析复合材料的力学性能和冲击试样断面的 SEM照片来探索硅烷 KH-560的最佳用量 。
6) One-step smelting reduction process
一步熔融还原
补充资料：熔融共混
分子式：
CAS号：
性质：又称熔体共混。将共混所需的聚合物组分在它们的黏流温度以上（>Tf）用混炼设备制取均匀聚合物共熔体，然后再冷却、粉碎或造粒的方法。设备主要有双辊混炼机、密闭式混炼机、挤出机等。该法的优点是对原料在粒度大小和均一怀方面的要求不像干粉共混法那样严格，所以原料准备操作较简单。熔融状态下，异种聚合物分子之间扩散和对流激化，加之混炼设备的强剪切作用，使得混合效果显著高于干粉共混，此外，它可能形成一部分接枝或嵌段共聚物，从而促进组分间的相容。
CAS号：
性质：又称熔体共混。将共混所需的聚合物组分在它们的黏流温度以上（>Tf）用混炼设备制取均匀聚合物共熔体，然后再冷却、粉碎或造粒的方法。设备主要有双辊混炼机、密闭式混炼机、挤出机等。该法的优点是对原料在粒度大小和均一怀方面的要求不像干粉共混法那样严格，所以原料准备操作较简单。熔融状态下，异种聚合物分子之间扩散和对流激化，加之混炼设备的强剪切作用，使得混合效果显著高于干粉共混，此外，它可能形成一部分接枝或嵌段共聚物，从而促进组分间的相容。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。