1) blending melt spinning
共混熔融纺丝
1.
Using PA6 and LDPE as raw materials, sea-island fibers with dpf of 5~6 dtex were prepared by blending melt spinning technology.
以尼龙6(PA6)和低密度聚乙烯(LDPE)为原料,采用共混熔融纺丝技术,制得单纤为5~6dtex的不定岛型海岛纤维,该纤维在后加工过程中通过苯减量可得到0。
2) melt spinning
熔融纺丝
1.
Review on the precursors of PAN based carbon fibers obtained from melt spinning;
熔融纺丝工艺制备碳纤维原丝
2.
Analysis of the frequency converting speed regulating system on melt spinning machine;
浅析熔融纺丝机变频调速系统
3.
Preparation of poly(ether sulfone)fiber via melt spinning process;
熔融纺丝法制备聚醚砜纤维
3) melt-spinning
熔融纺丝
1.
Synthesis and Melt-spinning of Polyferrocarbosilane as a Functional Silicon Carbide Precursor;
功能性碳化硅先驱体聚铁碳硅烷的合成及熔融纺丝
2.
Development of Preparing Hollow Fiber Membrane by Melt-spinning;
熔融纺丝制备中空纤维膜研究进展
3.
PP is through melt-spinning process then antibacterial and antistatic fibers are produced by melt spinning the blends of polypropylene and the antimicrobial agents and the antistatic agents.
选用钛酸酯偶联剂对纳米抗菌和抗静电混合粒子进行了表面修饰,并用透射电镜、接触角和红外光谱三种方法进行了表征,将经修饰的粒子与聚丙烯共混并熔融纺丝,考察了其纺丝及拉伸性能。
5) blend spinning
共混纺丝
1.
Disk type static mixer for blend spinning pack assembly and simulation experiment
共混纺丝组件用圆盘型静态混合器及模拟实验
2.
A series blend spinning polyester fiber are prepared by blend polyethylene terephthalate and additive agaent which contain sodium-5-sulfobis (β-hydroxyethyl) isophthalate (SIPE) at some proportion.
将含有间苯二甲酸双羟乙酯 5 磺酸钠(SIPE)成分的添加剂与聚酯共混纺丝形成系列共混聚酯纤维,其碱水解行为有别于传统的聚酯纤维:在一定温度下,它的碱减量率与时间之间呈现较好的线性关系,并且取决于初始碱浓度。
3.
In this paper, the ultra-fibre (fibril) formation in PP/PS(20/80)blend spinningprocess is introduced.
介绍了ＰＰ／ＰＳ（２０／８０）高分子混合系共混纺丝过程中，超细纤维（微纤）的形成。
6) melt blending
熔融共混
1.
PP/nano-Ti-alloy composites were prepared by melt blending of PP with nano-Ti-alloy.
将纳米钛合金与聚丙烯(PP)经熔融共混制得PP/纳米钛合金复合材料,研究了PP及其复合材料在大气暴露条件下的耐候性,利用傅立叶变换红外光谱仪分析了老化前后PP及其复合材料的化学结构。
2.
Poly(propylene carbonate)/polystyrene(PPC/PS) composites were prepared by melt blending followed by hot compression molding.
利用熔融共混的方法制备了聚丙撑碳酸酯/聚苯乙烯(PPC/PS)复合材料,并通过万能试验机、差示扫描量热分析仪(DSC)、热重分析仪(TG)以及扫描电子显微镜(SEM)分别研究了复合材料的力学性能、热性能及微观形态。
3.
The POE/PP composite was made through melt blending.
用熔融共混法制得了聚烯烃类弹性体(POE)/PP共混体系,研究了不同橡塑比对体系力学性能的影响;考察了不同填料(CaCO3,滑石粉,炭黑)对POE/PP复合材料性能的影响。
补充资料：共纺丝
分子式：
CAS号：
性质：由同一喷丝头纺出不同纤度、不同性质、不同断面形状的混合丝。用共纺丝加工的织物，有很好的蓬松性和手感，有特殊的光学效果和混色效果。纺丝方法有：(1)用同一块板上有不同孔结构的喷丝板纺丝；(2)用不同孔结构的板组装成组合喷丝板纺丝。可用于生产混合长丝或短纤维。是生产仿真丝、仿毛、仿麻、仿棉纤维的一种方法。
CAS号：
性质：由同一喷丝头纺出不同纤度、不同性质、不同断面形状的混合丝。用共纺丝加工的织物，有很好的蓬松性和手感，有特殊的光学效果和混色效果。纺丝方法有：(1)用同一块板上有不同孔结构的喷丝板纺丝；(2)用不同孔结构的板组装成组合喷丝板纺丝。可用于生产混合长丝或短纤维。是生产仿真丝、仿毛、仿麻、仿棉纤维的一种方法。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条