1) carbide morphology
碳化物形貌
1.
The effect of RE and heat treatment on eutectic carbide morphology and impact toughness of white cast iron was studied.
研究了稀土变质与热处理对白口铸铁的共晶碳化物形貌及冲击韧度的影响。
2.
The effects of improving white cast iron carbide morphology on the amount of modificator,solidification speed carbide equivalent,the time and temperature of modification such as other technological factor.
对白口铸铁采用稀土复合变质处理工艺进行了研究 ,试验了变质剂的加入量、凝固速度、碳当量、变质温度及时间等工艺因素对改善普通白口铸铁碳化物形貌的影响。
2) shape of the compound layer
化合物形貌
1.
The shape of the sample’s surface compound layer after nitrocarburizing with catalytic permeation was studied and the effect of test temperature,atmosphere and steel composition on the shape of the compound layer was discussed.
研究了催渗氮碳共渗后试样表面化合物的形貌 ,试验了温度、气氛及钢的成分对表面化合物形貌的影响 ,指出了预防化合物疏松的工艺措
3) morphology of coke deposits
积碳形貌
4) morphology of hydrated products
水化产物形貌
5) metal oxide morphology
金属氧化物形貌
6) carbide morphology
碳化物形态
1.
The results show that carbide morphology had obvious effect on the wear resistance.
结果表明，碳化物形态（大小、形貌、分布及数量）对莱氏体钢的耐磨性有明显影响。
2.
The influences of heating temperature on the carbide morphology of bainite in GCr15 steel are studied.
研究了加热温度对ＧＣｒ１５ 钢贝氏体中碳化物形态的影响，结果表明，加热温度越高，上贝氏体的碳化物的长条越短； 下贝氏体中的碳化物越呈点状分布，且点状更加粗化。
补充资料：碳化硅晶须补强碳化硅陶瓷基复合材料
分子式：
CAS号：
性质：以碳化硅陶瓷为基和以碳化硅晶须为增强剂的新型陶瓷材料。通过晶须的载荷转移、拔出及裂纹偏转作用，获得比普通碳化硅更高的强度和韧性。使用温度达1400℃。是一种重要的高温结构陶瓷。用于燃气轮机叶片等高温部件和耐磨件制造。采用原位生长工艺和烧结工艺制取。
CAS号：
性质：以碳化硅陶瓷为基和以碳化硅晶须为增强剂的新型陶瓷材料。通过晶须的载荷转移、拔出及裂纹偏转作用，获得比普通碳化硅更高的强度和韧性。使用温度达1400℃。是一种重要的高温结构陶瓷。用于燃气轮机叶片等高温部件和耐磨件制造。采用原位生长工艺和烧结工艺制取。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。