1) Zirconia sol
氧化锆溶胶
2) Zirconia Colloid Solution
二氧化锆溶胶
3) zirconium hydroxide sol
氢氧化锆溶胶
1.
The methods of preparing stable boehmite sol and zirconium hydroxide sol by anionic exchange method using inorganic compounds as raw materials were investigated in this dissertation,and forming-membrane capability of the sols were also investigated on the base of the it.
本论文主要研究了以无机盐为原料,采用离子交换溶胶-凝胶法制备稳定勃姆石溶胶和氢氧化锆溶胶的方法,并在此基础上对溶胶的成膜性进行研究。
4) zirconyl oxalate sol
草酸氧锆溶胶
1.
The colloid particle size and flow characteristics of zirconyl oxalate sol were investigated, and the performance of the membrane was characterized by SEM and gas-flow method.
本文以氧氯化锆为原料用Ｓｏｌ－Ｇｅｌ技术在多孔陶瓷管上制备了ＺｒＯ２膜，文中考察了草酸氧锆溶胶的粒子大小和流动特性；用ＳＥＭ、气体流动法等手段对氧化锆膜的结构、形貌与孔径大小分布进行了表征，并对膜的气体渗透性进行了考察。
5) zirconia solid solution
氧化锆固溶体
6) based solid solution
氧化锆基固溶体
补充资料：氧化锆-氧化钇红外陶瓷
分子式： ZrO2-Y2O3
CAS号：
性质：一种以二氧化锆为基体固溶6％～8％(mol)氧化钇的红外光学材料。立方晶结构。熔点2700℃。密度5.98g/cm3。红外透射波段1～10μm。采用1450℃以上高温烧结或1300～1700℃，50～300MPa热压制取。用于制造耐高温红外窗口和整流罩。
CAS号：
性质：一种以二氧化锆为基体固溶6％～8％(mol)氧化钇的红外光学材料。立方晶结构。熔点2700℃。密度5.98g/cm3。红外透射波段1～10μm。采用1450℃以上高温烧结或1300～1700℃，50～300MPa热压制取。用于制造耐高温红外窗口和整流罩。