1) ceria-zirconia solid solution
铈锆氧化物固溶体
1.
Preparation, characterization and three-way catalytic performance of ceria-zirconia solid solution;
铈锆氧化物固溶体的制备、表征及三效催化性能
2) cerium zirconium oxygen solid solution
铈锆氧固溶体
3) CeO 2-ZrO 2 solid solution
铈锆固溶物
1.
CeO 2-ZrO 2 solid solutions(Ce/Zr=1)prepared by co-precipitation and templating approach(filter paper is used as templating material),were used as supports for Pd catalysts.
以共沉淀法和滤纸作为模板剂的模板法制备铈锆固溶物 (Ce/Zr=1 )负载Pd催化剂 ,用XRD对其进行晶相分析 ,两种方法均形成立方萤石结构 。
4) supported ceria-zirconia solid solution
负载型氧化铈-二氧化锆固溶体
5) Ceria-Zirconia Solid Solution
铈锆固溶体
1.
The Synthesis of Ceria-Zirconia Solid Solution Optimized by Taguchi Design Method;
Taguchi设计法铈锆固溶体的优化合成
2.
Synthesis of ceria-zirconia solid solution for automotive exhaust treatment;
汽车尾气净化用铈锆固溶体合成方法
3.
Synthesis of butyl acetate catalyzed by ceria-zirconia solid solution under microwave irradiation;
微波辐射铈锆固溶体催化合成乙酸丁酯的研究
6) ceria-zirconia solid solutions
铈锆固溶体
1.
The research progress of the approaches for the preparation of ceria-zirconia solid solutions is reviewed.
对铈锆固溶体制备方法的研究进展进行了总结和评述。
补充资料：氧化锆基固溶体
分子式：ZrO2
CAS号：
性质：室温稳定的ZrO2是单斜相，在掺杂二价碱土金属氧化物或三价稀土氧化物后，形成萤石型立方固溶体，又称全稳定ZrO2，是氧离子导体。掺稀土比掺碱土金属者有更高的电导率，如在1000℃时，(ZrO2)0.88(CaO)0.12和(ZrO2)0.91(Y2O3)0.09的电导率分别为10-2和10-1S·cm-1。ZrO2基固溶体的离子迁移数近于1，但受氧分压影响，氧分压至一定下限时会出现电子电导。Y2O3稳定的ZrO2固溶体己成功地用作高温燃料电池和氧传感器的隔膜材料。
CAS号：
性质：室温稳定的ZrO2是单斜相，在掺杂二价碱土金属氧化物或三价稀土氧化物后，形成萤石型立方固溶体，又称全稳定ZrO2，是氧离子导体。掺稀土比掺碱土金属者有更高的电导率，如在1000℃时，(ZrO2)0.88(CaO)0.12和(ZrO2)0.91(Y2O3)0.09的电导率分别为10-2和10-1S·cm-1。ZrO2基固溶体的离子迁移数近于1，但受氧分压影响，氧分压至一定下限时会出现电子电导。Y2O3稳定的ZrO2固溶体己成功地用作高温燃料电池和氧传感器的隔膜材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。