1) antiphase boundary
反相畴界
1.
Theoretical investigation of Ni_3Fe antiphase boundary;
Ni_3Fe合金反相畴界结构和能量研究
2.
Calculation of the antiphase boundary and site preference in Fe_3Al;
Fe_3Al反相畴界及择优代位的对势计算
3.
Energy calculation of the antiphase boundary and stacking fault in intermetallic compound of Ni_3Al by MAEAM;
金属间化合物Ni_3Al反相畴界能及层错能的改进分析型嵌入原子法计算
2) antiphase domain boundary
反相畴界
1.
It is found by transmission electron microscope that the form of antiphase domain boundary has a strong effect on the ductility of ordered alloys.
利用透射电镜观察发现,反相畴界形态强烈影响合金的塑性。
3) anti phase boundary(APB)
反相畴界(APB)
4) Colony constitution
反相畴界APDB
5) inversion domain boundary
倒反畴界
6) antiphase domain
反相畴
1.
It can be seen that ceram melts partly and scatters and precipitates tiny ceramic phases under the action of high temperature by arc plasma,precipitated TiC presens namometer magnitude,and antiphase domain exsits in cladding,which is called plasma irradiation in.
在弧光等离子体高温作用下 ,陶瓷相TiC溶解、溃散及随后冷却时细小陶瓷相析出 ,析出的TiC呈纳米量级 ,且TiC中存在反相畴 ,称之为“等离子辐照反相畴” ,这是由等离子扫描的高能输入决定的。
2.
The antiphase domains of .
反相畴及出溶片晶是华中东部高压变质带中绿辉石的主要超微结构，出港片晶的大小受扩散速率和时间的控制，而反相畴的大小可作为变质温度和年龄的标志。
补充资料：反相畴界
反相畴界
antiphase domain boundary
雾爆赢及，黑黔辈之奎吵boundary单晶体中序合金中常观察到反相畴界。例如在CuZn合金的高温无序相中，Cu和Zn原子完全无规地分布在体心立方晶格的顶点和体心两种晶格位置上，两者完全等效，因一，1、。，，，，、、。。~~~~，一~、。一一，_，而(青)〔111]就是晶格平移矢量。在低温有序相中，j.叨、2产“古占~，Jy“~曰p，“’‘.少/、主。’协’幼巡’门尹J一“只”它们分别为Cu和Zn原子所占据，因此两种晶格位置不等效，肖〔 In:在有序合金中就不再是晶格平移一”J~，、2尹““‘“阵门尹J曰~’毋“一”~~朋川’‘.少矢量，作此平移就可以形成反相畴界，这是反相畴界的一种形成方式。在铁电体中也存在反相畴界。反相畴界的另一种形成方式是在固溶体从无序转变到有序过程中，在晶体中各个不同地点发生的有序小区域从成核到长大到彼此相遇而停止生长时，同位相者合并成一较大畴区，反位相者则形成畴界。 有序固溶体中，异类原子配对较同类原子配对具有更低的能量。但是，由于反相畴界的存在不改变键长和键角，虽然改变配位原子类型，界面能量不高，因而是有序固溶体中常见的一种界面。配位原子类型的变化可以不改变两类原子数之比，称保守界面;也可以改变两类原子数之比，而为非保守界面。后一种反相畴界的出现显然是容纳化学配比偏离的一种有效方式。 (吴希俊)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。