1) heat bending curve
高温变形曲线
1.
In this paper, retained strength of coated sand baked in the variant temperature were measured, fractures of all samples by application of SEM observation were analyzed, the heat bending curve of coated sand was measured.
测试了不同烘烤温度下覆膜砂的残留强度,利用扫描电镜观察并分析了各试样的断口形貌,测试了覆膜砂高温变形曲线。
2) temperature strain curve
温度-形变曲线
3) Temperature_strain curve of polymers
聚合物温度形变曲线
4) high temperature deformation
高温变形
1.
Lubrication action of pure aluminum during high temperature deformation of heat-resistant aluminum alloy;
纯铝在耐热铝合金高温变形过程中的润滑作用
2.
Study on the high temperature deformation mechanism of Ti-15-3 alloy;
Ti-15-3合金高温变形机制分析
3.
Dynamic recrystallization of vanadium microalloyed low carbon steel during high temperature deformation;
钒微合金化低碳钢高温变形动态再结晶
6) hot deformation
高温变形
1.
Research on the constitutive equation of Al_(18)B_4O_(33)w/AZ91D composite during hot deformation;
Al_(18)B_4O_(33)w/AZ91D复合材料高温变形力学本构方程研究
2.
Hot Deformation Behavior of Dual Phase Stainless Steel 00Cr21Ni2Mn5N;
00Cr21Ni2Mn5N双相不锈钢的高温变形
3.
The result indicates that the hot deformation of the ma.
结果表明,该材料在高温变形时的稳态流变应力与应变速率、变形温度均满足Arrhenius方程,其中更满足双曲正弦函数关系;该材料的热变形是受热激活控制的塑性变形过程。
补充资料：变形高温合金
变形高温合金
wrought superalloy
b lonx一ng gaowen heJ一n变形高温合金(wrought superalloy)能够通过热加工变形成型的高温合金材料。一般分为铁基变形高温合金、镍基变形高温合金和钻基变形高温合金3类。 铁基变形高温合金广泛用作燃烧室、涡轮盘、机匣和轴等零件，多数是从Fe一Cr一Ni系添加合金化元素发展起来的。中国发展此类合金的牌号较多，板材合金有GHi一40、GHlo15、GHioi6、GHZo18等;棒材合金有GHZ13o和GH23oZ;盘材合金有GHZ135、GH761等。一般适用于工作温度较低的发动机。 镍基变形高温合金发展较快，应用最广泛，一般以Ni一cr固溶体为基体添加多种合金元素发展起来的。此类合金，牌号甚多。中国自己研制成功的有GH151棒材合金;GHz7、GH3128、GH一70板材合金;GH4133盘材合金等。 钻基变形高温合金在中国发展较少，一般不研制新合金，这是因为钻资源缺乏。这类合金的焊接性能及抗热疲劳、抗氧化、抗冲刷和耐蚀等性能都较好，主要用于导向叶片。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。