1) XNBR
液体丁腈胶(XNBR)
2) carboxylated nitrile rubber(XNBR)
羧基丁腈橡胶(XNBR)
1.
The structure and dynamic mechanical properties of unpressed and pressed composites consisting of carboxylated nitrile rubber(XNBR) and hindered phenol compound 2,2′-methylenebis-(6-tertbutyl-4-methyl-phenol)(AO-2246) were investigated respectively.
将羧基丁腈橡胶(XNBR)和受阻酚2,2′-亚甲基双-(4-甲基-6-叔丁基苯酚)(AO-2246)混合制备出挤压和未挤压AO-2246/XNBR复合材料,并对其结构及动态力学性能进行了研究。
3) LNBR
液体丁腈橡胶
1.
Epoxy resin was modified with liquid nitrile-butadiene rubber(LNBR),and unidirectional boron fiber/epoxy resin(Bf/epoxy) composites were fabricated with compression molding.
对环氧树脂进行液体丁腈橡胶改性,并采用缠绕无纬布层压成型工艺制备了硼纤维/环氧单向复合材料。
2.
The plasticization of HNBR with liquid HNBR (LHNBR) was investigated and compared to that with liquid NBR (LNBR).
研究了液体氢化丁腈橡胶 (LHNBR)对氢化丁腈橡胶 (HNBR)的增塑效果 ,并且与液体丁腈橡胶 (LNBR)进行了比较。
4) CTBN
液体端羧基丁腈橡胶
1.
CTBN MODIFIED BMI CONSTRUCTION ADHESIVE (Ⅱ)THE FORM AND PROPERTIES OF CTBN MODIFIED 1~#/DACPE;
液体端羧基丁腈橡胶改性双马来酰亚胺结构胶粘剂(Ⅱ)DACPE固化BMI体系胶粘剂的改性及形态结构
2.
Aminopolysiloxane and carboxy terminal butadiene-acrylonitrile (CTBN) were used to modify the epoxy resin system, and the heat-resistant epoxy adhesive cured at room temperature was prepared.
采用氨基硅油和液体端羧基丁腈橡胶(CTBN)对环氧树脂进行化学改性,制备出室温固化耐热环氧胶粘剂。
5) CTBN
端羧基液体丁腈橡胶
1.
Dicyclopentadiene bisphenol diyanate ester(DCPDCE) was modified by CTBN to improve its brittleness.
采用端羧基液体丁腈橡胶(CTBN)对双环戊二烯型氰酸酯树脂(DCPDCE)进行改性。
6) hydroxyl-terminated polybutadiene/acrylonitrile rubber
端羟基液体丁腈橡胶
补充资料：端羧基液体丁腈橡胶
分子式：
CAS号：
性质：丁二烯和丙烯腈采用过氧化戊二酸为引发剂、无水酒精或四氢呋喃为溶剂，通过自由基聚合制备的液体橡胶。聚合温度110～120℃，聚合时间4～6h，转化率70％。端羧基液体丁腈橡胶以甲苯二异氰酸酯+三(2-甲基氮丙啶)氧化膦(TDI=MAPO)为固化剂，制成的推进剂黏结剂在220℃下测得的力学性能良好。在胺的催化作用下液体环氧树脂交联固化端羧基液体丁腈橡胶，可制得具有最佳强度的硫化胶。端羧基液体丁腈橡胶还广泛作为粘接、密封、灌封、喷涂材料。
CAS号：
性质：丁二烯和丙烯腈采用过氧化戊二酸为引发剂、无水酒精或四氢呋喃为溶剂，通过自由基聚合制备的液体橡胶。聚合温度110～120℃，聚合时间4～6h，转化率70％。端羧基液体丁腈橡胶以甲苯二异氰酸酯+三(2-甲基氮丙啶)氧化膦(TDI=MAPO)为固化剂，制成的推进剂黏结剂在220℃下测得的力学性能良好。在胺的催化作用下液体环氧树脂交联固化端羧基液体丁腈橡胶，可制得具有最佳强度的硫化胶。端羧基液体丁腈橡胶还广泛作为粘接、密封、灌封、喷涂材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。