1) aluminum and magnesium alloys
铝、镁合金
1.
The study situation of micro arc oxidation on aluminum and magnesium alloys was summarized and the growth mechanism of micro arc oxidation coatings was researched.
概述了铝、镁合金微弧氧化处理的研究现状 ,探讨了微弧氧化陶瓷层的形成机理。
2) Al-Mg alloy
铝镁合金
1.
The process of brushing Ni-P compound layer on Al-Mg alloy surface;
铝镁合金表面电刷镀镍-磷复合层的工艺研究
2.
Welding pipe of Al-Mg alloy;
铝镁合金管道的焊接施工
3.
The main materials of the ship made of aluminium are mainly used the hull planks of Al-Mg alloy (5083H226/H321) and the sec- tions of Al-Mg-Si alloy(6082-T2),and the welding technology for the hull is auto and/or semi-auto MIG welding as well as TIG welding(to weld tubes).
某公司承建的一艘全铝制船,其船体材料主要采用5083H116/H321铝镁合金板材与6082-T6铝镁硅合金型材。
3) Al-Mg alloy
铝-镁合金
4) aluminium-magnesium alloy
铝镁合金
1.
Dephosphorization of High Vanadium Steel and High Chromium Steel with Aluminium-Magnesium Alloy;
高钒钢高铬钢用铝镁合金脱磷
2.
The deoxidation ablity and desulphurization ablity of aluminium-magnesium alloy,changing inclusion properties of aluminium-magnesium alloy,transforming inclusion characters of aluminium-magnesium alloy and removing inclusion are analysed in thermodynamics.
从热力学上分析了铝镁合金脱氧、脱硫的能力和效果以及它对夹杂物的改质、变性、去除的作用,探讨了铝镁合金在钢水二次精炼中的加入方法及其残留物对钢质量的影响,得出它在钢水的二次精炼中具有很大的应用前景。
5) Al-Mg alloys
铝镁合金
1.
Under the same conditions,the Al-Mg alloys surface treatment was performed by the microarc oxidation with different components of electrolytes.
改变电解液的组成 ,在相同条件下进行铝镁合金表面的微弧氧化处理 ,用SEM/EDS手段观察氧化膜的形貌及对其成分分析并测量微弧氧化膜的厚度 ,根据锉刀试验评价氧化膜与基体的结合力 。
6) 5454 Al-Mg alloy
5454铝镁合金
1.
The corrosion behaviors and corrosion rate of seven metal materials in sea water, sea water - H2S corrosive media and industry cooling water were studied through experiment, which gave the order of the better material for sea water cooler: 2507 duplex steel→SUS321 →aluminum diffused steel→12Cr2AlMoV→20# carbon steel→07CrCuAlMoTi→5454 Al-Mg alloy.
在试验基础上探讨了七种金属在海水、海水-H2S腐蚀介质及工业循环水中的腐蚀行为和腐蚀速率,指出七种金属材料用于海水冷却器的耐蚀性排序为:2507双相钢>SUS321>固体粉末包埋渗铝>12Cr2AlMoV>20号碳钢>07CrCuAlMoTi>5454铝镁合金,进而对每种材料的应用效果进行了分析。
参考词条
补充资料：镁铝锌系铸造镁合金
镁铝锌系铸造镁合金
magnesium-aluminium-zinc cast magnesium alloy series
mellUxlnx一zhuzao melhej一n镁铝锌系铸造镁合金(magnesium一alumini-um一Zine east magnesium alloy series)以铝、锌为主要合金化元素的铸造镁合金，可用于砂型和金属型铸造，也可用于压力铸造，具有良好的流动性和焊接性能，热裂倾向性低，但有较大的显微疏松倾向。 中国牌号ZM一5(7.5%一9.0%Al，0.15%一0.5%Mn，0.2%一0.8%Zn，Mg为余量)合金，ZM一10(9 .0%~1 0.2%AI，0.15%一0.5%Mn，0.2%一0.8%zn，Mg余量)合金。zM一5合金为镁铝锌系铸造镁合金的代表，相当于前苏联牌号的M月5合金。合金中杂质为铁、铜、镍、硅、钻等，根据需要可适量加些被。 铝是主要合金化元素并含有锌和锰，通过改变铝、锌含量可改变合金的力学性能、铸造性能及抗蚀性能。铝含量的增加能进一步改善合金的铸造性能和提高合金的强度，但使伸长率和抗腐蚀性能降低。加入少量的锌和锰能显著提高合金的抗蚀性能，还可以提高合金的强度。但锌含量增加会使合金的缩松倾向增加。ZM一5合金的铸态组织由固溶体叔Mg)为基体，沿它的晶界以不连续网状分布着y(Mg‘A13)相，以及分布在固溶体叔Mg)中的Mn一Ai化合物小质点所组成。热处理强化常采用两种规范:(1)淬火(T4):加热到370~380℃保温2一4h，再升温至415士5℃保温12一16h，然后在空气中冷却。(2)淬火时效(T6):淬火后再在175士5℃人工时效16h。ZM一5合金的力学性能见表1。 表1 zM一5合金的力学性能详 镁铝锌系铸造镁合金结晶间隔较大，充型能力良好，铸造工艺性能及物理常数见表2。表2 zM一s合金铸造工艺性能及物理常数}牛粉粉{字朴 镁铝锌系铸造镁合金能铸出外形和内腔形状复杂的铸件，加之镁合金在汽油、煤油、润滑油中很稳定，因而多用于航空工业的燃油系统和润滑系统。还可作为在受冲击载荷时能吸收大量能量的零部件及飞机着陆轮的轮毅。 (杨朴)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。