1) ultra-fine equiaxed crystal
超细等轴晶粒
2) superfine equiaxed grain
超细等轴晶
3) equiaxed grain
等轴晶粒
1.
On the base of Mendelson s study, by which the three-dimensional size can be evaluated, the data of three-dimensional size distribution of equiaxed grain which is fitted to lognormal distribution and with the different value ofσandμis processed after partitioned into equal parts, then the random section is obtained by using emulation slicing, and then the r.
以Mendelson提出的三维尺寸评估方法为基础,对不同σ,μ值的等轴晶粒三维尺寸对数正态分布进行等区间数据处理,利用仿真切割方法得到随机截面,然后进行随机截线长度和其概率的计算,得到其随机截线分布并以此建立尺寸分布数据库。
2.
Based on the structural characterization described by Mendelson while evaluating three-dimensionalsize,the equal interval data processing was performed for the lognormal three-dimensional size distributionof equiaxed grain with different σ and μ values.
以Mendelson在评价三维尺寸时所描述的陶瓷结构特征为基础,对不同σ,μ值的等轴晶粒三维尺寸对数正态分布进行等区间数据处理。
4) superfine grain
超细晶粒
1.
The use of the die successfully produced superfine grain columnar material with average grain size as 1.
5μm的超细晶粒纯铜柱状材料,经实验分析,所获得超细晶粒纯铜的许多力学性能指标均得到了提高,抗拉强度从原来的235MPa提高到420MPa,硬度从114HV提高到184。
2.
The planking of superfine grain is made by the mold in laboratory,such as 5A02.
利用该模具,可以在实验室制备具有超细晶粒度的板状材料。
5) ultra-fine grain
超细晶粒
1.
The development of ultra-fine grain hot-rolled strips and wire rods in Anshan Steel Group was introduced.
主要介绍了鞍钢超细晶粒热轧卷板和线材的研制情况,总的研制思路是结合鞍钢设备的实际情况,探索低成本的超细晶粒钢的生产工艺路线。
2.
In order to research the microstructures and mechanical properties of hot rolling sheets with ultra-fine grain,influence of deformation temperature on austenite recrystallization grain size are studied through adopt GLEEBLE hot simulate test method.
为了研究碳素超细晶粒热轧钢板的显微组织及力学性能,采用GLEEBLE热模拟实验方法,研究了变形温度对奥氏体再结晶晶粒尺寸的影响,研究了冷却工艺和卷取工艺对铁素体晶粒细化的影响,探讨了热连轧过程中的变形诱导铁索体相变规律。
3.
The technical requirements of HRBF500E ultra-fine grain earthquake-resistant reinforced bar were analyzed.
分析了HRBF500E超细晶粒热轧抗震钢筋的技术要求。
补充资料：染料细粉及超细粉
分子式：
CAS号：
性质：非水溶性染料或不易溶染料常采用的剂型。如分散染料、还原染料等对粒度及粒度分布均有一定要求，要求相对集中，过细、过粗，均对使用有不良影响。染料生产企业对本企业的产品均作了规定。这些染料产品一般多在2μm到上到4μm范围内，如对某些分散染料要求控制在1μm左右，分散性能4～5级，还原染料也与分散染料近似，故有超细粉之称。为使染料产品达到上述细度，常采用万能粉碎机或砂磨、球磨等进行粉碎。
CAS号：
性质：非水溶性染料或不易溶染料常采用的剂型。如分散染料、还原染料等对粒度及粒度分布均有一定要求，要求相对集中，过细、过粗，均对使用有不良影响。染料生产企业对本企业的产品均作了规定。这些染料产品一般多在2μm到上到4μm范围内，如对某些分散染料要求控制在1μm左右，分散性能4～5级，还原染料也与分散染料近似，故有超细粉之称。为使染料产品达到上述细度，常采用万能粉碎机或砂磨、球磨等进行粉碎。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条