1) SnO_2/TiO_2
SnO2/TiO2
1.
SnO_2/TiO_2 antistatic nanopowders were synthesized by Sol-Gel method.
通过Sol Gel法合成SnO2/TiO2复合纳米抗静电剂,TEM分析和研究表明:抗静电剂粒子大小、分散性与SnCl2浓度、搅拌速度有关;抗静电剂的电阻率大小与SnO2与TiO2的配比有关;抗静电剂的颜色稳定性与原料配比有关。
2) TiO_2/SnO_2
TiO2/SnO2
1.
Based on preparation of SnO_2 sol by sol-gel method,nano-meter photocatalytic compound of TiO_2/SnO_2 was prepared and the atom ratio of titanium to tin on the surface is 85∶15(by XPS analysis).
在采用溶胶-凝胶法制备SnO2溶胶的基础上,制备出表面Ti/Sn原子比为85∶15(XPS全谱分析)的TiO2/SnO2复合体光催化剂;用于硫磷农药废水的降解,试验结果表明:复合体光催化剂比单一TiO2催化剂的催化活性要高,其原因是由于复合TiO2/SnO2催化剂中SnO2可接收电子,减少了TiO2电子-空穴对的复合,从而提高其催化活性。
2.
By incorporating stabilizing agent, catalyst into sol solution,TiO_2,SnO_2 and TiO_2/SnO_2 nano-crystalline powders were prepared by sol-gel method from inorganic and organic salts.
以有机、无机盐为原料,通过加入稳定剂、催化剂,采用溶胶 凝胶法制备TiO2、SnO2、TiO2/SnO2纳米微粒,采用XRD、SEM和XPS等技术对粒子性能进行分析。
3) SnO 2@TiO 2
SnO2@TiO2
4) tin dioxide-titanium dioxide
SnO2-TiO2
5) SO~(2-)_4/SnO_2-TiO_2
SO42-/SnO2-TiO2
1.
The synthesis of terpinyl acetate from terpineol and acetic anhydride with solid superacid SO~(2-)_4/SnO_2-TiO_2 as catalyst has been studied for the first time.
采用溶胶一凝胶法制备了新型复合固体超强酸SO42-/SnO2-TiO2,通过XRD和IR对其结构进行了表征。
6) TiSiW 12 O 40 /TiO2-SnO 2
TiSiW12O40/TiO2-SnO2
补充资料：CaO-TiO2-SiO2 ceramics
分子式：
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。