1) PMMA/SiO_2 aerogel
PMMA/SiO2气凝胶
2) PMMA/SiO 2 Hybrid quasi-gel
PMMA/SiO2杂化准凝胶
3) PMMA/SiO_(2) sol-gel composite glass
PMMA/SiO2溶胶-凝胶复合玻璃
4) SiO2 aerogel
SiO2气凝胶
1.
Using the obtained silica aerogels as raw materials,SiO2 aerogel/chitosan composite materials were prepared by an electrostatic effect.
采用常压干燥法制备了SiO2气凝胶,所得气凝胶为介孔结构,比表面积618。
2.
SiO2 aerogel doped CNTs with different contents were prepared using TEOS and CNTs as raw materials.
以正硅酸乙酯(TEOS)和碳纳米管(CNTs)为原料,采用溶胶-凝胶法和常压干燥法制备不同碳纳米管(CNTs)含量的SiO2气凝胶隔热材料。
3.
Nano-porous SiO2 aerogel insulations were prepared via two methods: (1) Using tetraethoxysilane (TEOS) as the precursor and followed by ethanol supercritical drying; (2) Surface modification of alcogels prepared from polyethoxydisiloxanes (E40) and followed by drying at ambient pressure.
以正硅酸四乙酯(TEOS)为硅源,通过溶胶凝胶及超临界干燥过程制备了SiO2气凝胶。
5) SiO_2-aerogel
SiO2气凝胶
1.
By using experimental method,the moisture absorption and desorption characteristic of SiO_2-aerogel(nano-structured material) was studied and was compared with silica gel.
对一种纳米级材料———SiO2气凝胶的吸、放湿性能及规律进行了实验研究,并与普通变色硅胶的调湿性能进行了实验比较。
6) SiO_2 aerogel
SiO2气凝胶
1.
After a reaction time of about 100min at room temperature, the silica sol was transformed into solgel, which was dried by supercritical drying technique to obtain wood-nano-SiO_2 aerogel.
在催化剂存在下,使正硅酸乙酯与乙醇-水溶液混合制备硅醇溶胶,迅速将其分别注入到西南桤木和紫椴木材中,令其在室温下反应100min左右得到木材-凝胶,然后采用超临界干燥技术制备木材-SiO2气凝胶。
2.
The SiO_2 aerogel/chitosan composite materials were prepared by ambient drying method under electrostatic effect.
用环境干燥法,通过静电作用制备了SiO2气凝胶/壳聚糖复合材料。
补充资料：Sds-聚丙烯酰胺凝胶电泳凝胶电泳
sds-聚丙烯酰胺凝胶电泳（sds-page，sodium dodecyl sulfate-polyacrylamide gel electrohoresis）
在有去污剂十二烷基硫酸钠存在下的聚丙烯酰胺凝胶电泳。sds-page只是按照分子大小分离的，而不是根据分子所带的电荷和大小分离的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条