说明:双击或选中下面任意单词,将显示该词的音标、读音、翻译等;选中中文或多个词,将显示翻译。
您的位置:首页 -> 词典 -> 氨基磺酸盐
1)  Sulfamate
氨基磺酸盐
1.
Study on synthesis and property of modified sulfamate superplasticizer;
改性氨基磺酸盐系高效减水剂的合成与性能研究
2.
Microstructure and texture in nickel shaped charge liner prapared by electroformation from sulfamate
氨基磺酸盐电铸镍药型罩的制备与微观组织
3.
The anodic behavior of electrolytic nickel anode in nickel sulfamate plating Solution was investigated,using anodic polarization curves,metallographic observation of cross-sections of nickel deposits,Hull Cell tests with solutions with and without Cl-,F-,bending tests with five solutions of different compositions,and sulfur content analysis in nickel deposit with mass spectrometry.
采用极化曲线、金相观察、赫尔槽电镀试验、弯曲试验和质谱分析方法,研究了氨基磺酸盐镀镍的阳极行为,证明了当在氨基磺酸盐镀液中使用电解镍阳极时,其活化峰值电流和镀液组成有很大的相关性,当镀液中不含F-和Cl-时其阳极活化峰值电流小,阳极处于极化状态,或相当大面积处于极化状态,使氨基磺酸根在极化的阳极表面氧化,从而使含硫化合物夹附于镀镍层,形成镀层内应力,并使镀层成为层状结构,并出现半光亮的外观。
2)  sulphamate ['sʌlfəmeit]
氨基磺酸盐
1.
Thus sulphamate electroplating technology was used to prepare nickel coating for the repair of the airplane parts.
氨基磺酸盐电镀镍工艺镀层内应力小、沉积速度快,且具有较好的结合力,可以很好地应用于飞机零件维修。
2.
Influence factors on internal stress of sulphamate NiFe alloy coating were approached experimentally.
实验探讨了氨基磺酸盐电沉积Ni-Fe合金层内应力的影响因素。
3.
In this paper,polarization behavior of electrodeposition of lead--cadmium and their alloys was studied in thesystem of sulphamate.
本文研究了氨基磺酸盐体系电沉积铅镉及其合金的极化行为,测定了在不同温度、搅拌、添加剂等因素对单金属镀液和混合镀液的极化曲线,表明添加剂间苯二酚对电沉积铅的极化影响较大,可实现铅镉共沉积的目的,初步研究了不同电流对合金镀层成分的影响。
3)  aminosulfonate
氨基磺酸盐
1.
Continuous, high speed and selective nickel plating on discrete parts in aminosulfonate bath;
分立器件连续高速选择氨基磺酸盐镀镍工艺
4)  sulfamate bath
氨基磺酸盐
1.
The experimental results show that Ni-Co alloy electrodeposit obtained from sulfamate bath possesses higher hardness and lower internal stress as comparred with that obtained from sulfate bath.
通过大量实验对比了氨基磺酸盐和硫酸盐两种电解液电沉积Ni-Co合金Co含量的影响因素,以及Ni-Co合金沉积层的硬度、内应力与Co含量的关系。
5)  aminosulfonic-based
氨基磺酸盐
1.
Effects of aminosulfonic-based superplasticizer on concrete durability;
氨基磺酸盐高效减水剂对混凝土耐久性的影响
2.
Study on Synthesizing Technology and Performance of Low-cost Modified Aminosulfonic-based Superplasticizer;
低成本改性氨基磺酸盐高效减水剂合成工艺与性能的研究
6)  sulfamate
氨基磺酸盐;氨基磺酸酯
补充资料:氨基磺酸和氨基磺酸盐


氨基磺酸和氨基磺酸盐
Sulfamie Aeid and Sulfamates

续表—一—一——一——r~一一一一—一一— 性质一数值———+—25C,在甲酞胺中25C,在甲醇中25C,在乙醇中(2%的苯)25C,在丙酮中25(.在乙醚中0 .1 6670 .04120 .01670 .0040 0001 氨基磺酸是具有氨基和磺酸基双官能团的物质,能够和多种无机、有机化合物进行各种化学反应。 (l)分解反应氨基磺酸在常温直至加热到熔点205C前都很稳定,当加热到209C时开始逐渐分解,继续加热至260七,就分解为二氧化硫、三氧化硫、氢气、氮气和水等。ZHS0sNHZ~~一,502十503+2H2十N艺+H20 (2)水解反应在室温下氨基磺酸水溶液很稳定,温度较高时则酸的溶液和按盐都水解为硫酸盐,如果提高温度,降低PH值和增加浓度,水解速率则迅速增大。水解反应是放热反应,氨基磺酸的浓溶液在密闭贮槽或没有良好放空装置的容器内加热时,能产生相当大的内压而引起容器破裂,浓度为60%(重量)的氨基磺酸铁水溶液,在pH~5加热到200℃或在pH一2加热到130C时,呈现急剧水解。然而,在具有良好放空装置容器内水解时,其危险性将减少到最低限度,因为60%(重量)的氨基磺酸按溶液在107C沸腾〔川。 水解反应的反应式如下:Q︺,,占一卜nUOC八U‘4 nUC︸‘l ....-R︺月,l︵fl内日,一 在不同浓度(%重量)硫酸中0 .0023 9147.537 1.8081.]796.310 25,在21.1%发烟硫酸中2。38妞签敬曲水溶液的困值与浓度关系(25℃时)fl一|nUn﹄i口口┌───────┬────────┐│pH浓度,m川/L │pH浓度,mol/L │├───────┼────────┤│1 .00().41 │{“·‘。‘.‘8 ││0 .75 0 50 │}。‘“5“‘, ││0 .50〔).63 │…“‘”‘2’”2││0 .25 0.87 │ │└───────┴────────┘HSO3NH:+H:O-一NH;HSO-NH月SoaNHZ+HZO一(NH峨)250刁在不同条件下,氨基磺酸的水解速率列于表4。表4氮基破酸在8。℃时的水解情况〔,‘〕·2·化学性质〔,。〕 氨基磺酸是比较强的酸,腐蚀性与其它酸如硫酸、硝酸和盐酸相比是较低的(见表3)。加入缓蚀剂后,还能够进一步降低腐蚀速率。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。