1) ammonium amidosulfate
氨基磺酸盐铝
2) sulphamate
['sʌlfəmeit]
氨基磺酸盐
1.
Thus sulphamate electroplating technology was used to prepare nickel coating for the repair of the airplane parts.
氨基磺酸盐电镀镍工艺镀层内应力小、沉积速度快,且具有较好的结合力,可以很好地应用于飞机零件维修。
2.
Influence factors on internal stress of sulphamate NiFe alloy coating were approached experimentally.
实验探讨了氨基磺酸盐电沉积Ｎｉ－Ｆｅ合金层内应力的影响因素。
3.
In this paper,polarization behavior of electrodeposition of lead--cadmium and their alloys was studied in thesystem of sulphamate.
本文研究了氨基磺酸盐体系电沉积铅镉及其合金的极化行为,测定了在不同温度、搅拌、添加剂等因素对单金属镀液和混合镀液的极化曲线,表明添加剂间苯二酚对电沉积铅的极化影响较大,可实现铅镉共沉积的目的,初步研究了不同电流对合金镀层成分的影响。
3) Sulfamate
氨基磺酸盐
1.
Study on synthesis and property of modified sulfamate superplasticizer;
改性氨基磺酸盐系高效减水剂的合成与性能研究
2.
Microstructure and texture in nickel shaped charge liner prapared by electroformation from sulfamate
氨基磺酸盐电铸镍药型罩的制备与微观组织
3.
The anodic behavior of electrolytic nickel anode in nickel sulfamate plating Solution was investigated,using anodic polarization curves,metallographic observation of cross-sections of nickel deposits,Hull Cell tests with solutions with and without Cl-,F-,bending tests with five solutions of different compositions,and sulfur content analysis in nickel deposit with mass spectrometry.
采用极化曲线、金相观察、赫尔槽电镀试验、弯曲试验和质谱分析方法,研究了氨基磺酸盐镀镍的阳极行为,证明了当在氨基磺酸盐镀液中使用电解镍阳极时,其活化峰值电流和镀液组成有很大的相关性,当镀液中不含F-和Cl-时其阳极活化峰值电流小,阳极处于极化状态,或相当大面积处于极化状态,使氨基磺酸根在极化的阳极表面氧化,从而使含硫化合物夹附于镀镍层,形成镀层内应力,并使镀层成为层状结构,并出现半光亮的外观。
4) aminosulfonate
氨基磺酸盐
1.
Continuous, high speed and selective nickel plating on discrete parts in aminosulfonate bath;
分立器件连续高速选择氨基磺酸盐镀镍工艺
5) sulfamate bath
氨基磺酸盐
1.
The experimental results show that Ni-Co alloy electrodeposit obtained from sulfamate bath possesses higher hardness and lower internal stress as comparred with that obtained from sulfate bath.
通过大量实验对比了氨基磺酸盐和硫酸盐两种电解液电沉积Ｎｉ－Ｃｏ合金Ｃｏ含量的影响因素，以及Ｎｉ－Ｃｏ合金沉积层的硬度、内应力与Ｃｏ含量的关系。
6) aminosulfonic-based
氨基磺酸盐
1.
Effects of aminosulfonic-based superplasticizer on concrete durability;
氨基磺酸盐高效减水剂对混凝土耐久性的影响
2.
Study on Synthesizing Technology and Performance of Low-cost Modified Aminosulfonic-based Superplasticizer;
低成本改性氨基磺酸盐高效减水剂合成工艺与性能的研究
补充资料：氨基磺酸
分子式 H2NSO2OH
CAS号 5329-14-6
性质 白色斜方晶系片状结晶，无臭，不挥发，不吸湿，可燃，低毒。相对密度2.216(20/4℃)。熔点205℃。在209℃时开始分解，在260℃下，本品会分解成二氧化硫、三氧化硫、氮和水等。折射率α型1.553，β型1.563，γ型1.568。溶于水和液氨，微溶于甲醇，不溶于乙醇和乙醚，也不溶于二硫化碳和液态二氧化硫。氨基磺酸的水溶液具有与硫酸、盐酸一样的强酸性。所有的普通盐（不包括钙、钡、铅盐）都不溶于水。
用途 用于分析化学，也可用于除革剂、防火剂、纸张和纺织品的软化剂、金属清洗剂等
毒性 本品低毒。对皮肤和眼睛有一定的刺激作用。生产设备应密闭，操作人员应穿戴好防护用具。
包装储运 采用塑料袋包装。贮存在阴凉通风干燥处，按一般化学品规定贮运。
CAS号 5329-14-6
性质 白色斜方晶系片状结晶，无臭，不挥发，不吸湿，可燃，低毒。相对密度2.216(20/4℃)。熔点205℃。在209℃时开始分解，在260℃下，本品会分解成二氧化硫、三氧化硫、氮和水等。折射率α型1.553，β型1.563，γ型1.568。溶于水和液氨，微溶于甲醇，不溶于乙醇和乙醚，也不溶于二硫化碳和液态二氧化硫。氨基磺酸的水溶液具有与硫酸、盐酸一样的强酸性。所有的普通盐（不包括钙、钡、铅盐）都不溶于水。
用途 用于分析化学，也可用于除革剂、防火剂、纸张和纺织品的软化剂、金属清洗剂等
毒性 本品低毒。对皮肤和眼睛有一定的刺激作用。生产设备应密闭，操作人员应穿戴好防护用具。
包装储运 采用塑料袋包装。贮存在阴凉通风干燥处，按一般化学品规定贮运。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条