2) zinc-phosphating
锌系磷化
1.
Aimed at the quality index of weld-neck-connection during 77B coiled-wire-rod online drawing,a fea- sible zinc-phosphating process at high temperature(for short:HZP)was developed.
结果表明,该锌系磷化液具有稳定性高、快速、少渣、使用寿命长和生产成本低等特点;经80℃×(10～15)min喷淋处理后,盘条焊接区可获得膜重>10g/m~2的优质磷化膜,其外观呈均匀黑色,结晶细致,附着牢固,抗蚀性好,能顺利拉拔,满足了当前高强度PC钢绞线原料——77B高碳盘条在线生产所提出的焊接头磷化质量及工艺操作要求。
3) Zinc phosphating
锌系磷化
1.
Effect of pickling on the quality of middle or low temperature zinc phosphating film
酸洗对中低温锌系磷化膜质量的影响
2.
In this paper,the composition of zinc phosphating solution used at environmental temperature was researched.
研究了配制锌系磷化液的配方:1 L溶液中加入磷酸100 mL,磷酸二氢钠20 g,氧化锌25 g,硫酸铜1 g,钼酸钠1 g,氟化钠1 g,酒石酸1 g。
4) zinc salt phosphating
锌盐磷化
1.
A new phosphating technology to meet the latest requirement of automakers is introduced,and the future development trend of zinc salt phosphating is discussed.
进入21世纪,为了不断提高汽车车身的防腐技术,要求进一步缩短磷化工艺时间、降低工艺成本,并使锌盐磷化技术更具环保性。
5) zinc-phosphated
锌磷化
补充资料：磷化锌
化学式Zn3P2，分子量258.08。深灰色四方晶体。有恶臭。密度 4.55g/cm3，熔点高于420℃。干燥时较稳定。在空气中易吸水分解，放出剧毒的磷化氢气体。不溶于醇，可溶于酸。跟水反应可生成磷化氢和联膦P2H4的混和物，这混和物在空气中能自燃。用作杀鼠剂，也可用作海上照明灯。由锌粉跟红磷在500～600℃时反应制得。