1) Zn-Mn system phosphating
锌锰系磷化
1.
A cleaning Zn-Mn system phosphating solution used in surface pretreatment of iron and steel at room temperature was developed in order to perform cleaning phosphating production at room temperature.
为使磷化实现清洁生产,开发了一种用于钢铁表面涂装前处理的清洁型常温锌锰系磷化液,实现了磷化液的所有分子均能参加成膜反应,且产物为磷化膜、水、沉渣或在磷化膜干燥过程中挥发物的设计思想。
2) zinc-manganese bonderizing
锌-锰系磷化
1.
Process,parameters and influence factors while applying ambient curing zinc-manganese bonderizing on bicycle surface are introduced.
介绍了自行车应用常温锌-锰系磷化的工艺过程、工艺参数及影响因素。
3) Zn 2+-Ca 2+-Mn 2+ phosphating
锌钙锰系磷化
5) zinc-phosphating
锌系磷化
1.
Aimed at the quality index of weld-neck-connection during 77B coiled-wire-rod online drawing,a fea- sible zinc-phosphating process at high temperature(for short:HZP)was developed.
结果表明,该锌系磷化液具有稳定性高、快速、少渣、使用寿命长和生产成本低等特点;经80℃×(10～15)min喷淋处理后,盘条焊接区可获得膜重>10g/m~2的优质磷化膜,其外观呈均匀黑色,结晶细致,附着牢固,抗蚀性好,能顺利拉拔,满足了当前高强度PC钢绞线原料——77B高碳盘条在线生产所提出的焊接头磷化质量及工艺操作要求。
6) Zinc phosphating
锌系磷化
1.
Effect of pickling on the quality of middle or low temperature zinc phosphating film
酸洗对中低温锌系磷化膜质量的影响
2.
In this paper,the composition of zinc phosphating solution used at environmental temperature was researched.
研究了配制锌系磷化液的配方:1 L溶液中加入磷酸100 mL,磷酸二氢钠20 g,氧化锌25 g,硫酸铜1 g,钼酸钠1 g,氟化钠1 g,酒石酸1 g。
补充资料：氧化铁锰锌
CAS：12645-49-7
中文名称：氧化铁锰锌
英文名称：Iron manganese zinc oxide；Manganese zinc ferrite；manganese zinc ferrate；manganese-zinc ferrite；ironmanganesezincoxide
中文名称：氧化铁锰锌
英文名称：Iron manganese zinc oxide；Manganese zinc ferrite；manganese zinc ferrate；manganese-zinc ferrite；ironmanganesezincoxide
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条