1) water embrittlement
水脆化
1.
Tensile strength and elongation of austempered ductile iron (ADI) were considerably reduced,resulting in remarkable water embrittlement under water adhesion condition.
水附着拉伸试验中,试样表面附着的水在试样塑性变形时分解出氢使奥贝球铁(ADI)产生氢脆,抗拉强度和伸长率显著下降,发生明显的水脆化现象。
2.
Influence of austempering temperature on water embrittlement behavior of austempered ductile iron (ADI) was studied.
研究了等温淬火温度对奥贝球铁 (ADI)水脆化行为的影响 ,水附着条件下不同等温淬火温度处理的ADI均发生水脆化行为 ,抗拉强度和伸长率显著降低 ;但随着等温淬火温度升高 ,ADI的水脆化程度降低。
3.
The result showed that both tensile strength and elongation of austempered ductile iron(ADI), pearlitic and quenched－ tempered ductile iron decreased drastically in condition of contact with water during tensile testing,exhibting remarkable water embrittlement of these materials.
研究了水附着对不同基体组织球铁的拉伸性能的影响，结果表明，水附着拉伸试验中，奥贝球铁、珠光体球铁、淬火回火球铁的拉伸强度和伸长率同时下降，发生显著的水脆化；而铁素体球铁几乎无水脆化现象 。
2) dehydration embrittlement
脱水脆化
3) embrittlement
[em'britlmənt]
脆化
1.
This study is concerned with the effect of post welding heat treatment(PWHT)on the microstructure and properties at the intercritical reheated coarse-grained heat-affected zone(IRCGHAZ)of WB36 steel, and investigated whether the PWHT could reduce IRCGHAZ embrittlement.
针对WB36钢(15NiCuMoNb5)临界再热粗晶区(IRCGHAZ)存在的脆化现象,研究了焊后热处理对模拟临界再热粗晶区(IRCGHAZ)组织性能的影响,探讨其改善韧性作用。
2.
The embrittlement in 1Cr21Ni5Ti duplex stainles s steel with medium titanium and aluminum content, the temperature range in whic h the toughness is sharply deteriorated has been determined and effect of soluti on temperature has been researched.
针对中限钛、铝的Cr21Ni5Ti双相不锈钢中发现的脆化现象,探索了脆化发生的温度范围以及脆化与固溶温度的相关性。
3.
The study wanted to solve the embrittlement problem in copper alloy due to bismuth in drinking water pipe,The result showed that the embrittlement of copper alloy can be completely avoided when Sn and P were added,A proportion of Cu-Bi 1 Sn 3 Zn 6 P 0.
为了解决因铋的加入引起的铜合金脆化问题,研究结果表明,通过添加元素Sn、P完全解决了因铋引起的脆化问题,并提出了配方Cu Bi1Sn3Zn6P0。
4) brittleness
[英]['britlnis] [美]['brɪtḷnɪs]
脆化
1.
Study on Mechanisms of Metal Material Brittleness under Vibration Cutting
金属材料在振动切削时脆化机理的研究
5) brittle
[英]['brɪtl] [美]['brɪtḷ]
脆化
1.
This article analyzes the reason for brittle of humidifier I.
分析了增湿器Ⅰ产生脆化现象的原因。
2.
From the aspects of mechanical properties, metallurgical analysis and process condition, the brittle causes of inner accessories used in flowing bed for itimeric cyanamide were analyzed in this article.
本文从化学成分 ,机械性能 ,金相分析 ,工艺条件等方面分析了三聚氰胺流化床内件脆化的原因 ,并提出了消除流化床脆化的措施。
6) brittleness
[英]['britlnis] [美]['brɪtḷnɪs]
脆性;脆化;脆弱
补充资料：脆脆小黑豆
脆脆小黑豆
材料：绿心黑豆，盐，糖，肉桂粉
做法：超级简单哦~~把绿心黑豆泡水4个小时，等豆豆胀大，沥干水分，放到小盒子里，加入盐，糖，肉桂粉，然后盖上盖子，甩甩甩，摇摇摇，让味道均匀裹在豆豆表面，接着，把豆豆平铺在盘子里，放到微波炉中，中火开5分钟后拿出，搅拌下，再平铺开，放入微波炉中，中火开3分钟后取出，放凉即可。
小贴士：
豆豆放到盘子当中一定要平铺，不然容易焦掉，而且烤的程度不均匀。
也可以把绿心黑豆换成去皮花生之类的~~黄豆我也试过，不过奇怪的是没有黑豆那么脆，有点软。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。