1) transverse cracking of matrix
基体横向开裂
2) transverse crack
横向开裂
1.
This article briefly introduces production process flow and its main equipments of seamless ERW pipe of 20 steel,and analyzes cause of transverse crack occurred in production of seamless ERW pipe of 20 steel,and gives out the main measures to solve transverse crack.
分析了20钢无缝化ERW焊管在生产过程中产生焊缝横向开裂的原因,提出了解决横向开裂的主要措施。
2.
A numerical iteration method with one-dimension nonlinear mechanical modeling was (created) to analyze the transverse cracking of continuously reinforced concrete pavement subjected to (temperature) and drying shrinkage with consideration of the nonlinear bond slip between steel bar and (concrete) and the (nonlinear) friction slip between concrete slab and subgrade.
考虑钢筋与混凝土之间的非线性粘结滑移关系及混凝土面板与地基之间的非线性摩阻滑移关系,采用数值迭代法建立了连续配筋混凝土路面在温缩和干缩作用下横向开裂的一维非线性力学分析方法,从而同时获得裂缝间距、裂缝宽度与钢筋应力3个设计指标的结果,编制了迭代法计算程序CRCPAP。
3) transverse cracking
横向开裂
1.
Sensitivity analysis of transverse cracking for continuously reinforced concrete pavement;
连续配筋混凝土路面横向开裂的敏感性分析
2.
Development laws of transverse cracking for continuously reinforced concrete pavement;
连续配筋混凝土路面横向开裂发展规律
3.
Talreja for study of transverse cracking in composite materials, a more reasonable method for calculation of the restricted coefficients is introduced, and used for study of transverse cracking in composite laminated plates.
在Talreja提出的研究复合材料横向开裂的损伤力学方法的基础上,文中引进了一种更合理的计算约束系数的方法,并将其用于研究复合材料叠层板的横向开裂,预估了其弹性模量的变化。
4) matrix transverse cracks
基体横向裂纹
1.
The form of the serials matrix transverse cracks was due to fiber bridging the matrix cracks and matrix stress distribution.
基体横向裂纹群的产生是由于纤维约束裂纹扩展、应力重新分布的结果,其间距与界面滑移强度有关。
5) seriak transverse matrix cracks
基体横向裂纹群
6) Matrix crack
基体开裂
1.
Matrix crack is one of the primary damages for composite pressure tank.
复合材料压力容器损伤破坏的主要形式之一是基体开裂,本文利用损伤力学方法中的细观力学对复合材料压力容器进行分析,采用等效夹杂法分析基体中任一点的应力情况,当应力达到临界值时基体开始产生裂纹,描述了基体开裂损伤的演化过程,建立裂纹密度和压力容器弹性模量之间的关系式,表现基体裂纹对压力容器刚度的影响。
2.
For matrix cracking and large deforming, the deformation of a filament wound case is analyzed and calculated.
本文分析计算了基体开裂及大变形对纤维缠绕壳体变形的影响，得到了比较满意的理论分析结果。
补充资料：穿晶开裂
分子式：
CAS号：
性质：金属材料开裂的金属学特征之一。裂纹由晶粒内部穿过。延性断裂的断口微观特征一般为韧窝状，脆性断裂的特征为解理或准解理花样。
CAS号：
性质：金属材料开裂的金属学特征之一。裂纹由晶粒内部穿过。延性断裂的断口微观特征一般为韧窝状，脆性断裂的特征为解理或准解理花样。