1) azides ion
叠氮离子
2) ion-nitriding
离子氮化
1.
The chromizing hardening process of carbon tool steel was studied by using double glow plasma surface chromizing process+ion-nitriding at 560℃.
采用离子氮化+双层辉光离子渗金属的复合处理渗铬新技术,对碳素工具钢进行560℃表面渗镀铬硬化研究。
2.
A chromized layer with good properties could be obtained in steel 45 with the ion-nitriding pre-heat treatment,and the chromized layer was composed of the phases Cr-(23)C_6,CrN,Cr/Fe,(Cr,Fe)_7C_3 and (Cr,Fe)_2N.
结果表明：离子氮化的预先热处理有助于实现610℃的低温盐浴渗铬,并得到良好的渗层,渗铬白亮层的相组成为Cr_(23)C_6、CrN、Cr/Fe、(Cr,Fe)_7C_3和(Cr,Fe)_2N等相。
3.
The surface treatments included electroplating hard chromium、ion-nitriding、and the newly developed ceramic hard film CrN, and compared the influence of different surface roughness on the pertormance of molding models surface roughness.
针对降低封胶模具与胶体间的粘模力来进行研究,以现在仍在使用的电镀硬铬、离子氮化,与蒸镀CrN陶瓷硬膜进行对比研究,探讨了不同表面粗糙度对封胶模具特性的影响。
3) plasma nitriding
离子渗氮
1.
Specialized production of plasma nitriding in China;
论离子渗氮的专业化生产
2.
Plasma Nitriding Assisted by Hollow Cathode;
空心阴极辅助离子渗氮研究
3.
Application of ion sputtering in plasma nitriding of austenitic stainless steel
离子溅射在奥氏体不锈钢离子渗氮中的应用
4) plasma nitriding
离子氮化
1.
The influence of plasma nitriding temperature on compound layer of passage plank;
离子氮化温度对通道板表面化合物层的影响
2.
It was found that the extent of the influence on plasma nitriding varies with different rare earth metal.
将纯稀土金属镧、铈、钕分别放入氮化炉中,对722M24钢进行离子氮化处理,用金相显微镜、扫描电子显微镜以及透射电镜观察和分析比较了稀土离子氮化和普通离子氮化氮化层的组织结构,发现在相同条件下,不同稀土元素对氮化影响是有区别的,其中铈、钕对离子氮化有一定的促进作用,可以抑制硬脆的Fe2-3N相形成,改善扩散层的脉状组织,但纯镧金属阻碍氮的扩散,抑制铁氮化物生成,降低扩散层深度,不利于加速氮化进程。
3.
The influence of pure rare earth addition on the plasma nitriding response of low alloy steel was investigated.
将纯稀土金属镧、铈、钕分别放入离子氮化炉中作为溅射源 ,对 72 2M2 4钢进行离子氮化 ,用扫描电镜进行了氮化表层物相的二次电子象观察 ,并用能谱仪、二次离子质谱仪、X射线衍射仪和辉光放电光谱仪对氮化表层进行了元素分析及物相结构分析 ,显微硬度计测量了加不同稀土氮化后沿氮化层的分布。
5) ion nitriding
离子渗氮
1.
Research on cyclic ion nitriding technology catalyzed by rare earth for 2Cr13 stainless steel;
2Cr13不锈钢的稀土催渗循环离子渗氮工艺研究
2.
Application of argon atmosphere ion nitriding in improving the thermal fatigue behavior of steel H13;
氩气氛离子渗氮提高H13钢热疲劳性能
3.
Wearability of 4Cr2MoWVNi and H11 die steels after ion nitriding;
4Cr2Mo WVNi与H11模具钢离子渗氮耐磨性能研究
补充资料：1,4-二叠氮-8-壬烯
CAS：177-11-7
分子式：C7H13NO2
分子质量：143.18
沸点：108-110℃
中文名称：1,4-二叠氮-8-壬烯
英文名称：1,4-dioxa-8-azaspiro[4.5]decane
分子式：C7H13NO2
分子质量：143.18
沸点：108-110℃
中文名称：1,4-二叠氮-8-壬烯
英文名称：1,4-dioxa-8-azaspiro[4.5]decane
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条