1) highly expanded graphite
高倍膨胀石墨
1.
The highly expanded graphite of 350 ml/g was prepared by a chemical method using natural flake graphite, acetic anhydride, oil of vitriol, potassium dichromate as rawmaterials.
以鳞片石墨、乙酸酐、浓硫酸、重铬酸钾为原料,采用化学氧化法制备了膨胀体积为350ml/g的高倍膨胀石墨。
2) Low sulphur and high times expanded graphite
低硫高倍数膨胀石墨
3) expanded graphite
膨胀石墨
1.
Preparation and conductive behavior of expanded graphite/poly-(ethylene terephthalate) conductive composites;
膨胀石墨/聚酯导电复合材料的制备与导电行为
2.
Application of expanded graphite in treatment of environmental pollution;
膨胀石墨在环境污染治理中的应用
3.
Adsorption and decoloration of acid dyes waste water with expanded graphite;
膨胀石墨对酸性染料废水的吸附脱色作用
4) expandable graphite
膨胀石墨
1.
Structure and Flame Retardance of Expandable Graphite Filled PP;
可膨胀石墨阻燃聚丙烯的结构与阻燃性能
2.
In this research,the KH-550 or NXT-105 modified expandable graphite,carbon fiber,and acrylonitrile butadiene styrene resin(ABS)were mixed to prepare a composite with better conductivity.
利用硅烷偶联剂和钛酸酯偶联剂对膨胀石墨进行了改性,将不同含量的膨胀石墨及碳纤维与丙烯腈-苯乙烯-丁二烯共聚物复合,制备了具有较好导电和力学性能的复合材料。
3.
Ammonium polyphosphate(APP) and expandable graphite(EG) have been used to improve flame retardancy of poly(ethylene-co-vinyl acetate)(EVA).
对聚磷酸铵(APP)和膨胀石墨(EG)协同阻燃乙烯-醋酸乙烯酯共聚物(EVA)及其阻燃机理进行了研究。
5) exfoliated graphite
膨胀石墨
1.
Chemical preparation of exfoliated graphite and factors affecting its quality;
膨胀石墨的化学制备法和影响其质量的因素
2.
Preparation of TiO_2-coated exfoliated graphite photocatalyst and its adsorption and photodegradation of methyl orange solutions;
膨胀石墨负载纳米TiO_2光催化剂的制备及对甲基橙溶液的吸附与光降解
3.
Preparations, structures and applications of exfoliated graphite;
膨胀石墨的制备、结构和应用
6) Graphite expansion
石墨膨胀
补充资料：膨胀石墨
分子式：
CAS号：
性质：又称柔性石墨。石墨经特殊化学处理，嵌入碱金属、卤素、金属卤化物、强氧化性含氧酸等形成层间化合物，再经高温处理急速分解，发生膨胀，体积可增至原来的几百倍。疏松多也，富有弹性。耐温范围宽，在-200～3600℃之间。能承受中子、γ-、β-等射线的长期照射。在高温、高压或辐射等条件下工作，不发生分解、变形或老化。化学性质稳定。可作密封元件，可在深冷氢气分离净化装置、硫酸回收装置、核能工业的硼酸泵等苛刻的条件下使用。还可作坩埚、保温、衬里、隔音和防震材料以及催化剂载体、吸附剂、脱色剂等。是有前途的新颖工程材料。缺点是强度还不够高。
CAS号：
性质：又称柔性石墨。石墨经特殊化学处理，嵌入碱金属、卤素、金属卤化物、强氧化性含氧酸等形成层间化合物，再经高温处理急速分解，发生膨胀，体积可增至原来的几百倍。疏松多也，富有弹性。耐温范围宽，在-200～3600℃之间。能承受中子、γ-、β-等射线的长期照射。在高温、高压或辐射等条件下工作，不发生分解、变形或老化。化学性质稳定。可作密封元件，可在深冷氢气分离净化装置、硫酸回收装置、核能工业的硼酸泵等苛刻的条件下使用。还可作坩埚、保温、衬里、隔音和防震材料以及催化剂载体、吸附剂、脱色剂等。是有前途的新颖工程材料。缺点是强度还不够高。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条