2) sulfur-free expandable graphite
无硫可膨胀石墨
1.
Preparation of sulfur-free expandable graphite by nitric acid;
用HNO_3制备无硫可膨胀石墨及影响因素探讨
3) low-sulfur expandable graphite
低硫可膨胀石墨
1.
It was found that the used oxidation-intercalation system could produce low-sulfur expandable graphite with good expandable property.
探索了 HCIO_4/H_2SO_4/KMnO_4/CH_3COOH 氧化插层体系制备低硫可膨胀石墨的新方法。
4) sulphur-free expanded graphite
无硫膨胀石墨
1.
Study on preparation of sulphur-free expanded graphite was made using nitric acid and phosphoric acid as steep in strong oxidizing environment.
以硝酸、磷酸为浸泡剂,在强氧化剂的作用下,对无硫膨胀石墨的制备进行了初步研究。
5) the flexible graphite in low sulphur compound
低硫膨胀石墨
6) low sulfur expansible graphite
低硫可膨胀石墨
1.
The low sulfur expansible graphite was prepared by reacting natural flake graphite with mixing solution made from sulfuric acid(98%), nitric acid(65%) and oxalic acid.
用硫酸（９８％）、硝酸（６５％）和草酸的混合液与天然鳞片石墨反应制备低硫可膨胀石墨，最佳反应条件是：石墨、硫酸（９８％）、硝酸（６５％）、草酸的重量比为１∶２。
补充资料：膨胀石墨
分子式：
CAS号：
性质：又称柔性石墨。石墨经特殊化学处理，嵌入碱金属、卤素、金属卤化物、强氧化性含氧酸等形成层间化合物，再经高温处理急速分解，发生膨胀，体积可增至原来的几百倍。疏松多也，富有弹性。耐温范围宽，在-200～3600℃之间。能承受中子、γ-、β-等射线的长期照射。在高温、高压或辐射等条件下工作，不发生分解、变形或老化。化学性质稳定。可作密封元件，可在深冷氢气分离净化装置、硫酸回收装置、核能工业的硼酸泵等苛刻的条件下使用。还可作坩埚、保温、衬里、隔音和防震材料以及催化剂载体、吸附剂、脱色剂等。是有前途的新颖工程材料。缺点是强度还不够高。
CAS号：
性质：又称柔性石墨。石墨经特殊化学处理，嵌入碱金属、卤素、金属卤化物、强氧化性含氧酸等形成层间化合物，再经高温处理急速分解，发生膨胀，体积可增至原来的几百倍。疏松多也，富有弹性。耐温范围宽，在-200～3600℃之间。能承受中子、γ-、β-等射线的长期照射。在高温、高压或辐射等条件下工作，不发生分解、变形或老化。化学性质稳定。可作密封元件，可在深冷氢气分离净化装置、硫酸回收装置、核能工业的硼酸泵等苛刻的条件下使用。还可作坩埚、保温、衬里、隔音和防震材料以及催化剂载体、吸附剂、脱色剂等。是有前途的新颖工程材料。缺点是强度还不够高。