1) temperature gradient technique (TGT)
温梯法
1.
A high quality sapphire single crystal oriented along (1102) was grown by the temperature gradient technique (TGT) and the crystal quality was investigated using X-ray rocking curve (XRC).
本文描述使用温梯法(TGT)生长(1102)方向的白宝石单晶,应用X射线双晶摇摆曲线(XRC)测定了晶体内部的完整性,再利用KOH熔体腐蚀出样品的r面(1102)上的位错蚀坑,借助扫描电子显微镜(SEM)进行观察,发现r面白宝石的位错腐蚀坑呈等腰三角形,并且有台阶状结构,并分析了位错的成因。
2.
High quality sapphire crystal oriented along [0001] was grown by the temperature gradient technique (TGT) and subsequently was fabricated into well double-polished (0001) sapphire wafers.
本文采用导向温梯法 (TGT)生长 [0 0 0 1 ]方向的白宝石晶体 ,利用气相传输平衡 (VTE)技术对晶体表面进行处理 ,发现双面抛光的C面白宝石晶片高温下与富锂 (Li2 O蒸气 )气氛发生反应 ,表面生成一层γ LiAlO2 ,随着VTE反应温度从 75 0℃下降到 730℃ ,γ LiAlO2 晶核的颗粒也随着减小 ,在 730℃时已在 1 μm以下 ,经稀盐酸 (HCl)腐蚀后形成多孔的表面 ,此方法有望制备出用于外延GaN的多孔衬
2) temperature gradient technique
温梯法
1.
apphire boules,120mm in diameter and 4kg in weight have been grown by temperature gradient technique(TGT).
应用温梯法生长出直径１２０ｍｍ，质量为４ｋｇ的白宝石晶体。
3) temperature gradient method
温度梯度法
1.
Tabular gem-grade diamond crystal synthesized with temperature gradient method at HPHT;
高温高压温度梯度法合成板状宝石级金刚石单晶
2.
When growing large diamond crystals by temperature gradient method under high temperature and high pressure,if all the diffused carbon source from higher temperature region cannot be absorbed by the seed crystals,the different present forms of superfluous carbon source,regrown graphite or diamond nuclei,would have great effects on the growth process of large diamond crystals.
温度梯度法生长宝石级金刚石单晶过程中,当籽晶无法完全吸收由高温端扩散下来的碳源时,多余碳源的不同析出形式(再结晶石墨或者自发核)对晶体生长速度有明显的影响。
3.
Large synthetic diamond was grown by temperature gradient method(TGM) under HPHT.
用高温高压温度梯度法作为实验手段来生长优质宝石级金刚石单晶。
4) temperature gradient technique
温度梯度法
1.
(001) γ-LiAlO_2 plates grown by temperature gradient technique (TGT) have been annealed in Li-rich and O_2 atmosphere at 1100 /70 h.
研究了温度梯度法生长的γ-LiAlO2晶体在1100℃下富Li气氛和空气中退火处理后的表面形貌、表面结构以及吸收光谱。
2.
Transparent and integrate calcium fluoride crystals, 75mm in diameter, were grown by temperature gradient technique (TGT) .
用温度梯度法成功生长了直径75mm、完整、透明的氟化钙晶体,对晶体进行了TG-DTA测试分析,确定了其熔点为1413。
3.
The growth of LiGaO 2 by temperature gradient technique (TGT) is reported.
以温度梯度法生长LiGaO2 晶体 ,通过形貌观察、X射线衍射分析和X射线光电子能谱分析确认在样品的中部形成了单一相的LiGaO2 晶体。
5) temperature gradient technique (TGT)
温度梯度法
1.
This paper studied the inclusion in the calcium fluoride crystals grown by temperature gradient technique (TGT).
本文对温度梯度法生长的氟化钙(CaF2)晶体中的包裹物进行了研究,用光学显微镜和SEM观察了包裹物的形貌,对晶体中的包裹物和透明部分作了微区EDX成分分析,对包裹物所含的杂质进行了解释,提出了减小或消除包裹物的措施。
2.
A transparent γ-LiAlO_2 crystal has been grown by temperature gradient technique (TGT).
利用温度梯度法生长出了透明的γ LiAlO2 单晶 ,通过扫描电镜和X射线薄膜衍射分析了不同退火气氛对所切得的 ( 0 0 1 )晶片表面结构的影响。