1) Metallurgy notch
冶金学缺口
2) metallurgical defects
冶金缺陷
1.
The results show that residual stress and serious metallurgical defects near the fracture initiation site are the failure cause of the gearbox output shaft.
利用金相检查、SEM分析和X射线衍射物相分析等方法,对材料为42CrMo钢的开裂大型齿轮箱输出轴进行失效分析,结果表明,残余拉应力和位于中心的严重的冶金缺陷是输出轴失效的原因。
2.
The result indicates that the metallurgical defects in the casting is the reason that cause the brittle fracture of the reinforced bars, and the change of the environmental temperature only has the function of catalysis.
对使用过程脆断的30MnSi高强钢筋的断口、金相组织和轧制状态下的母材以及连铸坯低倍组织进行了全面的检验和分析,检验结果表明,连铸过程中的冶金缺陷是诱发钢筋脆断的因素,而环境温度的变化只是起到催化的作用。
3.
Aiming at the current existing problems of study and fabrication of national aluminum sheet used for easy-open can without being pay more attention to the effects of intrinsic metallurgical defects, a new idea to link organically with hot deformation process in the study of the aluminum sheet used for easy-open can has been put forward by author.
针对目前我国铝材生产与研究中对内在冶金缺陷的影响作用重视不足、液态(熔体)处理与各种固态处理均是按各自系统独立进行研究的现状,作者结合本课题组的前期研究基础,以具有实用价值且量大面广的易拉罐用铝材(Al-Mn-Mg合金)作为研究对象,提出从改善铝材冶金质量这一关键技术入手,将铝材的处理状态(熔体处理和均匀化)与热变形加工有机地结合起来进行研究的新思路。
3) metallurgical defect
冶金缺陷
1.
The bolts was fractured after used for two years, resulting from bad working and serious metallurgical defects , such as segregation and inclusion.
结果表明:螺栓在服役2 a后就发生了断裂,主要是因为螺栓加工不良和钢中存在严重的偏析与夹杂物等冶金缺陷;在交变拉应力作用下,使得螺栓在螺纹沟处发生脆性疲劳断裂。
2.
The metallurgical defects,such as high density inclusion and low density inclusion,always appear in the titanium alloys,which are the fatigue crack sources in the titanium components and lower the application life of the components.
钛合金铸锭中经常出现高密度夹杂和低密度夹杂等冶金缺陷,这种夹杂缺陷成为钛合金零部件的疲劳裂纹源,降低零部件的使用寿命,用于航空发动机,可能引起机毁人亡的重大灾难。
3.
The experimetal results show that the premature break of drive gear shaft is attributed to the metallurgical defect in raw 20CrMo steel and abnormal structure present in hardened case as well as lower core hardness.
结果表明,驱动齿轮轴的过早断裂系原材料冶金缺陷、表面硬化层组织反常和心部硬度偏低所致。
4) metallurgy defects
冶金缺陷
1.
WEDM crackle is posterity defects, which causes the presence of waster and extra manufacture costs, so effective methods must be used to eliminated material metallurgy defects and WEDM crackle, then, die quality and life cycle can be improved largely, manufacture costs can be lowered, and competency can be increased, these changes bring good economic benef.
模具钢原材料冶金缺陷是先天性不足,是导致模具寿命短和早期失效致命伤。
2.
The metallurgy defects of 6063 alloy are discussed.
讨论了该合金的一些冶金缺陷及消除方法。
5) financing gap
资金缺口
1.
According to the national policy targets, the financing gap for urban wastewater infrastructure construction in China’s prefecture-level cities and municipalities during the 11th Five Year Plan period was estimated.
根据国家相关政策目标,估算了"十一五"期间我国地级及以上城市的污水设施建设资金的缺口情况,分析了资金缺口及由此形成的地方财政负担随城市所处区域、经济水平及人口规模变化而表现出来的分布特征,在此基础上提出了"十一五"时期城市污水设施建设投资策略建议。
6) financial gap
金融缺口
1.
Study on the cause of financial gap about non-state-owned enterprises and the countermeasures;
非国有企业金融缺口的成因及对策的研究
2.
Research on the Rural Financial Gap based on ARMA:Taking Anhui as an Example
基于ARMA模型的农村金融缺口预测研究——以安徽为例
补充资料：紧缩缺口与膨胀缺口
紧缩缺口又称通货紧缩缺口，指充分就业条件下，社会实际投资低于社会储蓄的空缺，亦即社会总供给超过社会总需求的差额。它表现为社会对商品和劳务需求的价值低于在充分就业条件下能够生产的价值。例如，在充分就业的情况下，国民生产总值为22000亿美元，而此时社会总需求即总投资加上总消费为20000亿美元，这意味着留下了2000亿美元的通货紧缩缺口。根据乘数原理，它会导致收入更大幅度的下降。但稍增加投资，又可实现充分就业。因此，当存在通货紧缩缺口时，只有通过增加政府开支或通过政策鼓励，帮助私人投资，才能便社会实现充分就业。
膨胀缺口又称通货膨胀缺口，是指在充分就业经济中投资超过储蓄的差额，即社会总需求超过社会总供给的差额。表现为社会对商品和劳务需求的价值超过在充分就业条件下所能创造的国民生产总值。例如，在充分就业条件下，国民生产总值为20000亿美元，而此时的社会总需求即总投资加上总消费为22000亿美元，即意味着存在2000亿美元的通货膨胀缺口。这种差额或缺口会导致物价上涨。由于这一差额往往又是由通货膨胀造成的，故称为通货膨胀缺口。
虽然膨胀缺口是紧缩缺口的反面，但它对就业和生产的影响与紧缩缺口的影响并不完全相反。紧缩缺口可以造成生产和就业的进一步下降;但膨胀缺口决不可能使就业超过充分就业所限制的水平，因此，膨胀缺口在非充分就业下会使物价和就业都有所增加，而在充分就业条件下就会导致纯粹的通货膨胀。
膨胀缺口又称通货膨胀缺口，是指在充分就业经济中投资超过储蓄的差额，即社会总需求超过社会总供给的差额。表现为社会对商品和劳务需求的价值超过在充分就业条件下所能创造的国民生产总值。例如，在充分就业条件下，国民生产总值为20000亿美元，而此时的社会总需求即总投资加上总消费为22000亿美元，即意味着存在2000亿美元的通货膨胀缺口。这种差额或缺口会导致物价上涨。由于这一差额往往又是由通货膨胀造成的，故称为通货膨胀缺口。
虽然膨胀缺口是紧缩缺口的反面，但它对就业和生产的影响与紧缩缺口的影响并不完全相反。紧缩缺口可以造成生产和就业的进一步下降;但膨胀缺口决不可能使就业超过充分就业所限制的水平，因此，膨胀缺口在非充分就业下会使物价和就业都有所增加，而在充分就业条件下就会导致纯粹的通货膨胀。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条