Higher NH_3 concentration led to the formation of the incoherent and unfastened film,and higher S~(2-) and Cd~(2+) concentration tend to increase the size of CdS colloidal particles,but increasing S~(2-) and Cd~(2+) concentration ratio([S~.
在相同NH3摩尔浓度下,随着S2-和Cd2+摩尔浓度比值([S2-]/[Cd2+])的增大,CdS胶体粒子粒度减小;透过光谱的峰位随着胶体粒子尺寸的减小向短波方向移动,当NH3摩尔浓度变化时,在一定的范围内改变CdS膜的透过率。
2.
The results show that, when overbased calcium alkyl salicylate samples are subjected to aging reaction, the size of colloidal particles in samples decreases, the relative content of calcium hydroxide in colloidal particles increases, the viscosity of samples decreases and the total basicity number of samples increases.
结果表明:老化反应后高碱度烷基水杨酸钙胶体粒子变小,胶体中氢氧化钙的相对含量增加,粘度降低,总碱值(TBN)升高;老化后样品的清净性及抗磨性明显提高;水、甲醇及氢氧化钙等影响老化效
3.
It has been found there are different the best ratio of water in different process,and the colloidal particles size is smaller and homogeneous in the best ratio of water to calcium oxide,while the chemical structures of them were similar.
利用FE EM(冷冻蚀刻电镜 )、傅立叶红外分析 (FT IR)等方法对高碱度烷基水杨酸钙两种制备工艺中水量的影响进行考察 ,结果发现 ,不同工艺中有不同的最佳水量 ,最佳水量下产品中的胶体粒子较小、分布比较均匀 ,且化学结构相似 ,并对作用机理进行推
3) Colloidal particles
胶体粒子
1.
A summarization of the interaction of colloidal particles and trace metal in natural water;
天然水体中胶体粒子与痕量金属相互作用研究
2.
By summarizing the exchange adsorption effects of suspended particles in natural water(including colloidal particles) on trace metal,the paper mainly introduces the components of suspended particles and the mechanism effect of each component on trace metal.
综述了自然水体中悬浮颗粒物(包括胶体粒子)对痕量金属的吸附交换作用,重点介绍了悬浮颗粒物的组成成分及各组成成分对痕量金属的作用机理。
3.
It has been found that the product produced in higher polarity solvent such as xylene has smaller and homogeneous colloidal particles,while the product produced in the lower polarity solvent such as heptane has bigger and inhomogeneous colloidal particles.
考察了高碱度烷基水杨酸钙制备中溶剂的影响 ,结果发现 :在极性较大的二甲苯溶剂中制备的产品胶体粒子尺寸较小 ,分布比较均匀 ;而在极性较小的庚烷中合成的产品胶体粒子尺寸较大 ,分布不均。
4) colloid particles
胶体粒子
1.
Cross-linking and fixing the shell,the novel capsule "colloidosome",which is composed of a close-packed shell of colloid particles,can be fabricated.
胶体粒子在乳滴表面自组装形成有序的球面胶体壳,交联固定乳滴表面的胶体粒子制备新型的"胶体体(colloidosome)"微胶囊,即以胶体粒子为壳的微胶囊。
5) PS colloidal crystal
PS胶体晶体
6) PS-AA latex nanosphere
PS-AA胶体球
1.
The as-prepared PS-AA latex nanospheres are of a core-shell structure,as revealed by phosphoric acid staining.
甲苯能对PS-AA胶体球进行原位选择性溶解。
补充资料：初级粒子和原级粒子
分子式：
CAS号：
性质：又称初级粒子和原级粒子。利用各种化学反应方法得到的最初粒子(晶粒)。一次粒子的大小约为0.005～1μm，比筛分的极限小得多，在介质中有相当高的稳定性。
CAS号：
性质：又称初级粒子和原级粒子。利用各种化学反应方法得到的最初粒子(晶粒)。一次粒子的大小约为0.005～1μm，比筛分的极限小得多，在介质中有相当高的稳定性。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条