3) TiO_2 film
二氧化钛膜
1.
The TiO_2 film was prepared by means of Cathodic electrodeposition, and the effect of the deposition conditions to the properties of the TiO_2 film were discussed in this paper.
采用阴极电沉积法制备二氧化钛膜,并讨论沉积条件对二氧化钛膜的影响。
4) TiO2 thin film
二氧化钛薄膜
1.
Coating the TiO2 Thin Film on the Active Carbon with CVD and Photo-Catalytic Degradation of Acid Violet Red;
用CVD法在活性炭上镀二氧化钛薄膜光催化降解酸性品红
2.
The results show that TiO2 fine particle appeared anatase structure in TiO2 thin films,and formed the composite phase structure of anatase,rutile and Brookit of TiO2 powders.
实验结果表明:溶胶的陈化时间、膜的热处理温度、涂膜层数等都将直接影响二氧化钛薄膜的紫外可见光谱和禁带宽。
5) titania film
二氧化钛薄膜
1.
The results of SEM and TF-XRD indicate that a titania film layer with anatase and rutile structure was formed on the surface of NiTi SMA after oxidized with hydroxyl radical (·OH) as an oxidant.
通过高级氧化法对NiTi形状记忆合金进行表面改性,SEM和TF-XRD分析证实,羟自由基(·OH)氧化后的NiTi形状记忆合金表面生成了金红石和锐钛矿结构的二氧化钛薄膜。
6) ordered porous TiO2 film
二氧化钛多孔膜
1.
Three-dimensionally ordered porous TiO2 films were prepared by sol-dipping method using silica spheres multilayer templates.
以该阵列为模板,通过在TiO_2前驱体溶胶中多次浸渍热处理循环,随后采用超声辅助的NaOH溶液腐蚀去除硅球模板,制备了>20层厚的反转结构的二氧化钛多孔膜。
补充资料：包膜二氧化钛
分子式：
CAS号：
性质：是指颗粒表面经过用某些氧化物或有机化合物包膜的二氧化钛。经表面处理的二氧化钛其表面性质将视包膜物的种类和数量的不同，其某一方面的应用性能会得到提高，成为适应不同应用领域的品种。同时，耐久性和分散性都有所提高。通常采用的是湿法包膜，即将未包膜二氧化钛作成浆状，然后加入相应水溶性金属盐溶液，调整pH值，使相应水合氧化物包覆在二氧化钛粒子表面。经过滤、洗涤、干燥和粉碎制成表面处理的二氧化钛，有机物包膜多在粉碎过程中加入。无机包膜物主要是铝、硅、钛、锆的氧化物，有机包膜物可以是醇胺、有机硅、表面活性剂等。
CAS号：
性质：是指颗粒表面经过用某些氧化物或有机化合物包膜的二氧化钛。经表面处理的二氧化钛其表面性质将视包膜物的种类和数量的不同，其某一方面的应用性能会得到提高，成为适应不同应用领域的品种。同时，耐久性和分散性都有所提高。通常采用的是湿法包膜，即将未包膜二氧化钛作成浆状，然后加入相应水溶性金属盐溶液，调整pH值，使相应水合氧化物包覆在二氧化钛粒子表面。经过滤、洗涤、干燥和粉碎制成表面处理的二氧化钛，有机物包膜多在粉碎过程中加入。无机包膜物主要是铝、硅、钛、锆的氧化物，有机包膜物可以是醇胺、有机硅、表面活性剂等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条