1) surface treated ti-tanium dioxide
包膜二氧化钛
4) TiO_2 film
二氧化钛膜
1.
The TiO_2 film was prepared by means of Cathodic electrodeposition, and the effect of the deposition conditions to the properties of the TiO_2 film were discussed in this paper.
采用阴极电沉积法制备二氧化钛膜,并讨论沉积条件对二氧化钛膜的影响。
5) coated TiO2
包核二氧化钛
1.
Through comparison of different preparation technologies of coated TiO2,the title technology with nano rutile TiO2 colloid was explored.
通过几种不同包核二氧化钛制备方法比较,进行了纳米金红石型二氧化钛胶体制备包核二氧化钛工艺过程的探索,结果表明:采用我国储量丰富的低价的矿石粉(如高岭土、硅石粉、云母粉、碳酸钙、硫酸钡等)作为包核二氧化钛的内核原料,以纳米金红石型二氧化钛胶体为包核主原料,工艺简单,成本低,环保治理简便,废水经处理后可循环使用,产品品质优良,白度、遮盖力、吸油量等性能指标接近二氧化钛标准,能替代二氧化钛应用于涂料、造纸、橡胶和塑料等领域。
6) TiO2 thin film
二氧化钛薄膜
1.
Coating the TiO2 Thin Film on the Active Carbon with CVD and Photo-Catalytic Degradation of Acid Violet Red;
用CVD法在活性炭上镀二氧化钛薄膜光催化降解酸性品红
2.
The results show that TiO2 fine particle appeared anatase structure in TiO2 thin films,and formed the composite phase structure of anatase,rutile and Brookit of TiO2 powders.
实验结果表明:溶胶的陈化时间、膜的热处理温度、涂膜层数等都将直接影响二氧化钛薄膜的紫外可见光谱和禁带宽。
补充资料：包膜二氧化钛
分子式：
CAS号：
性质：是指颗粒表面经过用某些氧化物或有机化合物包膜的二氧化钛。经表面处理的二氧化钛其表面性质将视包膜物的种类和数量的不同，其某一方面的应用性能会得到提高，成为适应不同应用领域的品种。同时，耐久性和分散性都有所提高。通常采用的是湿法包膜，即将未包膜二氧化钛作成浆状，然后加入相应水溶性金属盐溶液，调整pH值，使相应水合氧化物包覆在二氧化钛粒子表面。经过滤、洗涤、干燥和粉碎制成表面处理的二氧化钛，有机物包膜多在粉碎过程中加入。无机包膜物主要是铝、硅、钛、锆的氧化物，有机包膜物可以是醇胺、有机硅、表面活性剂等。