1) nylon 1313
尼龙1313
1.
Wide-angle X-ray diffraction(WAXD) has been used to investigate the structural parameters of the solid state of nylon 1313 annealed at different temperatures.
通过W AXD对尼龙1313的结晶结构以及晶型间的相互转变进行了研究,发现尼龙1313在常温下结晶易形成γ晶型,当热处理温度升至110℃时,晶型转变为α晶型。
2) petroleum fermentative nylon1313
石油发酵尼龙1313
3) nylon
[英]['naɪlɔn] [美]['naɪlɑn]
尼龙
1.
Study of Property of Reinforced and Toughened Nylon 66 Special Compound for Auto Industry;
增强增韧尼龙66汽车专用料的性能研究
2.
Progress in Study of Polyolefin-g-MAH/Nylon Alloy;
马来酸酐接枝聚烯烃／尼龙共混合金的研究进展
3.
Development and applications of long carbon chain nylon;
长碳链尼龙的研究开发与应用
4) PA
[英][,pi: 'eɪ] [美]['pi 'e]
尼龙
1.
Preparation and Characterization of PA6/Layered Double Hydroxide Nano-meter Composite;
尼龙6/水滑石纳米复合材料的制备与表征
2.
Improving Toughness and Abrasion Performance of PA by Blending Modification;
尼龙的增韧耐磨共混改性
3.
It introduced the study progress on PA toughened by modified EPDM at home and abroad,analyzed the influencing factors during toughening PA with modified EPDM,such as graft ratio,content of rubber,crystallizability of PA etc.
介绍了国内外改性EPDM增韧尼龙研究进展,分析了在改性EPDM增韧PA过程中的影响因素,如接枝率、橡胶含量、PA的结晶性能等,阐述了EPDM增韧PA的机理,最后展望了该领域的发展趋势和方向。
5) Polyamide
[英][pɔli'æmaid] [美][,pɑli'æm,aɪd]
尼龙
1.
Progress in Studies of Polyamide/Carbon Nanotubes Composites;
尼龙/碳纳米管复合材料研究进展
2.
Pretreatment for electroplating of polyamide (PA) substrates
尼龙(PA)电镀前处理
3.
The latest studies on modification of polyamide are summarized.
尼龙是重要的工程塑料,对其进行改性可以得到性能多样的产品,拓宽其应用领域。
6) PA6
尼龙
1.
Research on Application of Censpheres in Modification of PA6 by Glass Fiber;
空心微珠在玻纤改性尼龙(PA6)中的应用研究
2.
Silica microspheres containing different concentrations of nano-meter silver particles were prepared with silver nitrate, dehydrated alcohol, TEOS, aqueous ammonia and sodium borohydride as raw materials, and which was then blended with PA6 to prepare PA6/(Ag/SiO_2) antistatic composite.
以硝酸银、无水乙醇、正硅酸乙酯(TEOS)、氨水、硼氢化钠为原料,通过溶胶凝胶法制备了载有纳米银的二氧化硅粒子,并将其与尼龙6共混,得到了抗静电的尼龙/(Ag/Si02)复合材料。
补充资料：尼龙1313
分子式：
CAS号：
性质：又称聚酰胺1313(polyamide 1313)或尼龙1313(nylon 1313)。相对密度1.01，熔点170～174℃，拉伸强度35～37MPa，弯曲强度33～43MPa，冲击强度250～290kJ/m2，洛氏硬度59～62，吸湿率(浸水24h)0.137％～0.175％，表面电阻率1015Ω，体积电阻率1014Ω·cm。由十三碳二胺和十三碳二酸缩聚制备。加工性好、宜作电缆护套，也可增强填充改性。
CAS号：
性质：又称聚酰胺1313(polyamide 1313)或尼龙1313(nylon 1313)。相对密度1.01，熔点170～174℃，拉伸强度35～37MPa，弯曲强度33～43MPa，冲击强度250～290kJ/m2，洛氏硬度59～62，吸湿率(浸水24h)0.137％～0.175％，表面电阻率1015Ω，体积电阻率1014Ω·cm。由十三碳二胺和十三碳二酸缩聚制备。加工性好、宜作电缆护套，也可增强填充改性。