1) perpendicular magnetic anisotropy
垂直磁各向异性
1.
The results show that sputtering Ar gas pressure has a great effect on the microstructure, perpendicular magnetic anisotropy and the coercivity of [Co 85 Cr 15 /Pt] 20 multilayers.
研究结果表明 ,Ar溅射气压对 [Co85Cr1 5 Pt]2 0 多层膜的微结构、垂直磁各向异性和矫顽力有重要的影响 。
2.
The results show that the nanowire arrays are amorphous with a perpendicular magnetic anisotropy and high coercivity H_c=3.
利用x射线衍射仪、透射电子显微镜、振动样品磁强计和穆斯堡尔谱仪研究了样品的结构和磁性,发现纳米线阵列是非晶结构,且拥有垂直磁各向异性和高的矫顽力,Hc=3·04×104A/m。
3.
And the origin of the perpendicular magnetic anisotropy in these films was studied.
理论分析结果表明 ,TbCo非晶垂直磁化膜的垂直磁各向异性主要来自于Tb离子的非球对称分布电荷与膜内晶场之间的库仑相互作用以及膜内的应力。
2) strong perpendicular magnetic anisotropy
强垂直磁各向异性
3) perpendicular anisotropy
垂直各向异性
1.
All the samples show strong perpendicular anisotropy and the perpendicular coercivity(H_(c⊥)) reaches the maximum 138kA/m as x=11nm.
样品垂直方向的矫顽力在x=11nm时达到最大,为138kA/m,平行于膜面方向的矫顽力基本上与x的变化无关,且所有的样品都显示出很强的垂直各向异性。
2.
The nano-multilayer films have large perpendicular anisotropy and high coercive force than the TbDyFe single layer film, and show giant magnetostrietive effect though they have perpendicular anisotropy.
尽管纳米多层膜样品具有垂直各向异性,但仍具有超磁致伸缩性能。
3.
The Co/Pt multilayers with perpendicular anisotropy are the potential and promising elements in design of perpendicular high density storage media, It have stimulated increasing interests.
具有垂直各向异性的Co/Pt多层膜作为很有发展前景的垂直磁记录介质,引起了人们的研究兴趣。
4) perpendicular magnetic anisotropy
垂直各向异性
1.
In this paper, we report the observation of exchange bias in (Pt/Co)-n/FeMn multilayer with perpendicular magnetic anisotropy.
采用磁控溅射方法制备了以Pt为缓冲层和保护层的具有垂直各向异性(Pt/Co)n/FeMn多层膜。
5) Vertical anisotropy
垂直各向异性
1.
The results show that high magnetic performance CoNiMnP permanent magnet films with vertical anisotropy could be fabricated with electric current density less than 10mA/cm2 and pH 3～4 at room temperature.
采用电镀法制备了与微电子CMOS工艺兼容的硅基CoNiMnP垂直各向异性永磁薄膜,并对该薄膜的微结构、组成、磁性能等进行了分析与测试。
2.
The results show that high magnetic performances CoNi 1-x Nd x MnP permanent magnet films with vertical anisotropy can be fabricated with current density less than 10 mA·cm -2 at room temperature.
2mm的硅片上设计并制备了 2 0 0 0个大小为 5 0 μm× 5 0 μm的CoNi1 -xNdxMnP垂直各向异性永磁薄膜阵列 ,并对该薄膜陈列的组成、磁性能等进行了分析与测试。
6) perpenticular magnetic anisotropy
垂直膜面各向异性
补充资料：磁各向异性
| 磁各向异性 magnetic anisotropy 物质的磁性随方向而变的现象。主要表现为弱磁体的磁化率及铁磁体的磁化曲线随磁化方向而变。铁磁体的磁各向异性尤为突出，是铁磁体的基本磁性之一。磁各向异性来源于磁晶体的各向异性。温度低于居里温度（见铁磁性）的铁磁体受外磁场作用时，单位体积物质达到磁饱和所需的能量称为磁晶能，由于晶体的各向异性，沿不同方向磁化所需的磁晶能不同。对每种铁磁体都存在一个所需磁晶能最小和最大的方向，前者称易磁化方向，后者称难磁化方向。铁磁体受外力作用时，由于磁弹性效应（见磁致伸缩），体内应力和应变的各向异性会导致磁各向异性。在外磁场或应力作用下的铁磁体进行冷、热加工处理时，均可产生感生磁各向异性。铁磁薄膜材料在一定外界条件影响下进行晶体生长时，也会引入生长磁各向异性。 |