1) magnetic anisotropy
磁各向异性
1.
Element-specific in-plane magnetic anisotropy in Co_(0.9)Fe_(0.1) films;
Co_(0.9)Fe_(0.1)薄膜面内元素分辨的磁各向异性
2.
Thermal annealing at 100℃ shows that large perpendicular magnetic anisotropy and coercivity still remain after annealing,inverse magnetostrictive anisotropy and coercivity still remain after annealing,inverse magnetostrictive anisotropy is one part of perpendicular magnetic anisotropy and responsible for the decrease of coercivity.
10 0℃退火表明 ,薄膜保留较大的垂直磁各向异性、矫顽力和很好的矩形比 ,磁致伸缩各向异性是引起矫顽力下降的主要原因。
3.
The magnetic anisotropy constants of the samples with various grain size were obtained by the studies of collecti.
通过对集体磁激发现象的研究，得到了不同颗粒尺寸的α－Ｆｅ_２Ｏ_３超微粒的磁各向异性能常数。
2) transverse magnetic anisotropy
横向磁各向异性
1.
The theoretical results of multilayered film with transverse magnetic anisotropy show that, the maximum impedance occurs when magnetic field is close to the effective anisotropy field at high frequencies, smaller resistivity of the conducted layer would lead to a larger impedance change ratio in multilayered film.
对于单轴横向磁各向异性多层膜，理论计算结果表明：高频阻抗在某一外加磁场（近似等于等效各向异性场）下出现最大值，铁磁层和导电层电阻率相差较大的多层膜中将出现较强的巨磁阻抗效应。
3) magnetic anisotropy
磁性各向异性
1.
The magnetic anisotropy of polycrystalline materials can be predicted by averaging the properties of monocrystals weighted by using orientation distribution function (ODF).
利用多晶材料织构取向分布函数(ODF)对单晶性质进行加权平均可有效预估其宏观磁性各向异性。
4) magnetoelastic anisotropy
磁弹性各向异性
5) magnet anisotrophy
磁各向异性性
6) perpendicular magnetic anisotropy
垂直磁各向异性
1.
The results show that sputtering Ar gas pressure has a great effect on the microstructure, perpendicular magnetic anisotropy and the coercivity of [Co 85 Cr 15 /Pt] 20 multilayers.
研究结果表明 ,Ar溅射气压对 [Co85Cr1 5 Pt]2 0 多层膜的微结构、垂直磁各向异性和矫顽力有重要的影响 。
2.
The results show that the nanowire arrays are amorphous with a perpendicular magnetic anisotropy and high coercivity H_c=3.
利用x射线衍射仪、透射电子显微镜、振动样品磁强计和穆斯堡尔谱仪研究了样品的结构和磁性,发现纳米线阵列是非晶结构,且拥有垂直磁各向异性和高的矫顽力,Hc=3·04×104A/m。
3.
And the origin of the perpendicular magnetic anisotropy in these films was studied.
理论分析结果表明 ,TbCo非晶垂直磁化膜的垂直磁各向异性主要来自于Tb离子的非球对称分布电荷与膜内晶场之间的库仑相互作用以及膜内的应力。
补充资料：磁各向异性
| 磁各向异性 magnetic anisotropy 物质的磁性随方向而变的现象。主要表现为弱磁体的磁化率及铁磁体的磁化曲线随磁化方向而变。铁磁体的磁各向异性尤为突出，是铁磁体的基本磁性之一。磁各向异性来源于磁晶体的各向异性。温度低于居里温度（见铁磁性）的铁磁体受外磁场作用时，单位体积物质达到磁饱和所需的能量称为磁晶能，由于晶体的各向异性，沿不同方向磁化所需的磁晶能不同。对每种铁磁体都存在一个所需磁晶能最小和最大的方向，前者称易磁化方向，后者称难磁化方向。铁磁体受外力作用时，由于磁弹性效应（见磁致伸缩），体内应力和应变的各向异性会导致磁各向异性。在外磁场或应力作用下的铁磁体进行冷、热加工处理时，均可产生感生磁各向异性。铁磁薄膜材料在一定外界条件影响下进行晶体生长时，也会引入生长磁各向异性。 |