1) Rare Earths salt
稀土氯化盐
1.
The activity coefficient of Rare Earths salt ErCl_3、DyCl_3、NdCl_3 and YCl_3 in H_2O solvent at 298K is determined by conductivity method,the molar conductivity of Rare Earths salt in H_2O is calculated as well as the activity coefficient of Rare Earths salt with Debye-Hücker and Osager-Falkenhangen formula.
应用电导法测定了298 K时4种稀土氯化盐 ErCl3、DyCl3、NdCl3 和 YCl3 在极性水溶剂中的电导率,计算了稀土氯化盐的摩尔电导率,利用Debye Hücker和Osager Falkenhangen公式计算了稀土氯化盐在水中的活度系数。
2.
In this paper, we applied in activity coefficient of Rare Earths salt YCl_3 in DMF and H_2O with conductivity method at 298K, and discussed the effect of concentration on activity coefficient of electrolyte solution.
应用电导法测定了298K时稀土氯化盐YCl3在混合溶剂(DMF-H2O)中的活度系数,并分析了浓度对稀土盐溶液活度系数的影响。
2) rare earth chloride
氯化稀土
1.
Synthesis of tributyl citrate with mixed rare earth chlorides as catalyst;
用混合氯化稀土催化合成柠檬酸三丁酯
2.
The separation was achieved on AS9 anion separation column with sodium carbonate mobile phase,the detection was performed by a conductivity detector,quantitative analysis was conducted with a calibration curve by measuring the peak area,then sulphate content was calculated,that is the determination of sulphate content in rare earth carbonate and rare earth chloride.
0mmol/LN a2CO3为流动相,以标准曲线法为定量方法,测定碳酸稀土和氯化稀土中硫酸根离子的含量。
3.
The effects of different rare earth chlorides, epoxides, molar ratio of epoxide/LnCl_3, monomer concentration, molar ratio of ε-CL/LnCl_3, polymerization temperature and time on the polymerization of ε-CL were investigated.
在离子液体中进行了无水氯化稀土催化ε己内酯(εCL)的开环聚合,并考察了不同氯化稀土、环氧化物、环氧化物/氯化稀土摩尔比、单体浓度、单体/氯化稀土摩尔比、反应温度和时间对聚合的影响。
3) ReCl_3
氯化稀土
1.
To improve conductivity and corrosion resistance of phenol formaldehyde resin(PF),PF was improved by copolymerization and blending with ReCl_3 and graphite as modifying agent.
为了提高酚醛树脂的导电和耐腐蚀性能,分别利用石墨和氯化稀土作为改性剂,通过在酚醛聚合过程中以及在聚合后掺混的方式对酚醛树脂进行改性,改性后的酚醛树脂应用于燃料电池双极板后,大大提高了双极板的体积电导率,同时提高了双极板的力学强度和耐腐蚀性。
4) rare earths salt solution
稀土氯化盐水溶液
1.
With the increasing concentration of rare earths salt solution,the conductivity proportion of rare earths salt in the solution got higher and the molar conductivity of rare earths salt got lower.
应用电导率仪在298K下测定4种稀土氯化盐ErCl3,DyCl3,NdCl3和YCl3在极性水溶剂中的电导率,利用公式计算稀土氯化盐的摩尔电导率,并讨论了浓度对稀土氯化盐水溶液电导率和摩尔电导率的影响,稀土氯化盐水溶液随浓度的增加,电导率逐渐升高,摩尔电导率逐渐减小。
5) rare-earth salt lanthanum chloride (LaCl_3·3H_2O)
稀土盐三氯化镧(LaCl_3·3H_2O)
6) lanthanide chloride
稀土氯化物
1.
Synthesis and characterization of complexes of(Me3Si)2NSiMe2 functionized cyclopentadienyl lanthanide chloride are reported.
采用无水无氧Schlenk技术合成了三种含(Me3Si)2NSiMe2取代茂基稀土氯化物。
2.
The Diels-Alder reaction of butadiene with maleic anhydride can bc catalyzed by various lanthanide chloride under mild conditions with satisfactory yield, The activities of the catalysts are greatly dependent on the atomical number of the lanthanide of the catalysts.
本文报道以丁二烯和顺丁烯二酸酐为原料,用7种简便易得的稀土氯化物催化这一Dies-Alder反应的结果。
补充资料：熔盐氯化法生产四氯化钛
熔盐氯化法生产四氯化钛
production of titanium tetrachlo-ride by molten salt chlorina-tion process
rongyon}UhuafO shengehon silUhuatai熔盐抓化法生产四抓化钦(produetion of ti-tanium tetraehloride by molten salt ehlorina-tion process)细粒富钦物料和石油焦在氯化炉内熔盐中与氯气作用生成四氯化钦的过程，为四氛化铁制取方法之一。所用富钦物料主要有铁渣或金红石。熔盐由碱金属氯化物(NaCI、KCI)和碱土金属氯化物((1a C12、MgC12)组成。此法的炉生产能力高、氯化温度较低，适用于各种富钦物料的氯化。 1954年，苏联索里雅克夫(e.n.eo月6，Ko。)和拜别柯夫(M.K·Ban反KoB)等提出用熔盐氯化钦渣生产Ticl;的方法，1961年实现了工业化生产，经不断改进后，已在前苏联普遍应用，并达到生产过程自动控制的程度。中国从80年代开始亦有用熔盐氯化法生产TIC14的。 原理富钦物料的熔盐氯化是在气(氯气)一固(物料)一液(熔盐)三相体系中进行的，反应过程复杂。当氯气流以一定流速由炉底部喷入熔盐后，对熔盐和反应物料产生强烈的搅动作用，并分散成许多细小气泡由炉底部向上移动。悬浮于熔盐中的细物料在表面张力作用下粘附于熔盐与氯气泡的界面上，随熔盐和气泡的流动而分散于整个熔体中，为在高温下进行氯化反应创造了良好条件。反应产物TICI、和沸点较低的组分(SICI;、AIC13、FeCI:等)及非冷凝性气体(CO、CO:等)，以气态从熔盐中逸出进入冷凝分离系统;高沸点氯化物(MgCIZ、CaCIZ、FeCI:等)则残留在熔盐中，使熔盐组成及其物理化学性质逐渐发生变化。因510:的氯化率较低，大部分以固体渣形态在熔盐中积令 生产TICI;用熔盐氮化炉示意图 1钢壳;2炉衬‘3一水冷却管;4一石墨电极;5加料孔; 6混合炉气出口;7一防雄阀;8一熔盐上排口;9熔盐; 10一通氛口累。 熔盐的物理化学性质(表面张力、粘度等)随其组成不同而变化，并对氯化过程产生重要影响。具有并使之保持较低表面张力和粘度的盐系，对反应物料的润湿性能好，可减少熔盐流动阻力和增强氯气泡的活动性，这是维持正常熔盐氯化反应的必要条件。此外盐系还要具有较大的密度，使反应物料不易沉积。 熔盐中存在的少量氯化铁，在参与氯化反应时起着传递氯的催化作用，使TIO:的氯化速度明显提高。 熔盐氮化炉炉体(见图)有圆形和长方形两种。加料口位于炉子上侧部(熔池上方)，通氯口位于炉底部(见彩图插页第24页)。氯化产物混合炉气由炉顶部排出，废熔盐由炉侧部前床或炉底部排出。氯化炉余热可由炉顶喷淋TICI;浆液及装在炉墙内的水冷导热管导出。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。