1) hybrid waterborne emulsion
复合水基微乳液
2) waterborne emulsion
水基微乳液
1.
In this work, the polystyrene was modified to sulfonated polystyrene ionomer(SPS) and was emulsified to a stable polymer waterborne emulsion by using the technology of phase inversion.
将聚苯乙烯制成磺化聚苯乙烯离聚体,利用相反转技术,将磺化聚苯乙烯离聚体制成具有纳米级稳定的水基微乳液,利用磺化聚苯乙烯颗粒内部作为反应场所,引发另一单体丙烯酸丁酯聚合,制备聚丙烯酸丁酯/磺化聚苯乙烯复合水基微乳液。
3) SPPO
水基微乳液
1.
The lightly sulfonated poly(phenylene oxide) (SPPO) ionomers in different mixing solvents were emulsificated by water to form a series of waterborne microemulsions.
以乙酰磺酸为磺化剂制备了磺化度为３～１７ｍｏｌ％的磺化聚苯醚（ＳＰＰＯ）并中和成盐，在一定的温度和搅拌速度下，加水将ＳＰＰＯ乳化成水包油的稳定水基微乳液。
2.
Sulfonated poly(phenylene oxide)(SPPO) ionomers in different mixing solvents were emulsified by water to form a series of waterborne microemulsions.
以乙酰磺酸为磺化剂制备了磺化度为３ ～１７ ｍｏｌ％ 的磺化聚苯醚（ＳＰＰＯ） ，并中和成盐，在一定的温度和搅拌速度下，加水将ＳＰＰＯ 离聚体溶液乳化成水包油的稳定水基微乳液。
3.
In this article,the lightly sulfonated poly(phenylene oxide)(SPPO)ionomers in different mixing solvents were emulsificated by water to form a series of waterborne microemulsions,The principle of emulsification was explained,The aggregated structure of SPPO chains in organic solvents was discussed.
以乙酰磺酸为磺化剂制备了磺化度为 3%～ 1 7%mol的磺化聚苯醚 (SPPO)并中和成盐 ,在一定的温度和搅拌速度下 ,加水将SPPO乳化成水包油的稳定水基微乳液。
4) waterborne microemulsion
水基微乳液
1.
The lightly sulfonated poly(phenylene oxide)(SPPO) ionomers in DMSO/CHCl3 mixed solvents were emulsified by water to form a series of waterborne microemulsions.
以乙酰磺酸为磺化剂制备了磺化度摩尔分数为３％～１７％的磺化聚苯醚（ＳＰＰＯ），在一定的温度和搅拌速度下，加水将ＳＰＰＯ离聚体溶液乳化成水包油的稳定水基微乳液。
2.
The lightly sulfonated poly(phenylene oxide) (SPPO) ionomers in different mixing solvents were emulsificated by water to form a series of waterborne microemulsions.
在一定的温度和搅拌速度下 ,加水将SPPO离聚体溶液乳化成水包油的稳定水基微乳液。
5) SPS
水基微乳液
1.
Waterborne emulsions of lightly sulfonated polystyrene ionomer(SPS) were prepared by neutralizatioin with ammonia liquor and addition of water.
在一定的温度和搅拌速率下，加水将ＳＰＳ乳化成水包油的稳定水基微乳液。
2.
Waterborne emulsions of lightly sulfonated polystyrene ionomer (SPS) were prepared by neutralization with ammonia liquor and addition of water.
将聚苯乙烯改性制成磺化聚苯乙烯离聚体，溶解在甲苯／甲醇混合溶剂中，缓慢加水将聚苯乙烯乳化成稳定的水包油的水基微乳液。
6) waterborne nanocomposite emulsion
水基纳米复合乳液
补充资料：复合乳液聚合
分子式：
CAS号：
性质：又称种子(乳液)聚合，两阶段(或多阶段)乳液聚合，核-壳乳液聚合或复合乳液聚合。为了得到颗粒较大的聚合物，在乳液聚合中，可先加入乳液作为种子，这样在聚合过程中，单体可在加入的种子上继续聚合，而不形成新的微粒，因此可以得到颗粒较大的聚合物，这种聚合称为种子聚合。首先，通过常规的(一般为间歇式)乳液聚合或乳液共聚合制备种子胶乳，然后在种子胶乳存在下进行另一种单体或单体混合物的聚合。是新近发展起来的一种乳液聚合方法。主要用来合成各种具有不同组分以及不同形态特征的复合聚合物胶乳。