1) foamed Al-Si alloy
泡沫铝硅合金
1.
In this paper, the internal friction of foamed Al-Si alloy(ZL104) in different bending modes was investigated, for getting the characteristics of the internal friction of foamed metal in different boundary conditions.
为了获得不同边界条件下泡沫金属的内耗特征,通过采用动态机械分析仪在不同弯曲模式下对泡沫铝硅合金的内耗进行实验研究。
2) foamed aluminum alloy
泡沫铝合金
1.
In this article an element model of foamed aluminum alloy is created by finite element analysis software .
用有限元分析软件ANSYS建立泡沫铝合金的模型 ,模拟出在高温条件下泡沫模型的背火面温度场分布情况 ,得出其温度分布规律并求出它的耐火极限。
3) aluminum alloy foam
泡沫铝合金
1.
The effects of rare earths on the foaming process and corrosion resistance of aluminum and aluminum alloy foam have been investigated,and the relationship between the rare earths' content and the corrosion resistance of the aluminum and aluminum alloy foam has also been discussed.
研究了稀土对泡沫铝及泡沫铝合金泡沫化和压缩性能的影响,讨论了稀土加入量和泡沫铝及泡沫铝合金耐腐蚀性能的关系。
2.
The cell-size effect on compressive properties of aluminum alloy foam is analysed.
在分离式霍普金森压杆(SHPB)和MTS810材料试验机上对多组孔径、多组密度的开孔泡沫铝合金(AA6101)材料进行了准静态与动态压缩实验研究。
4) foam Al-alloys
泡沫铝合金
1.
Study on Technology of Making Foam Al-alloys;
泡沫铝合金制备工艺研究
2.
Property characteristic of foam Al-alloys of penetrating casting around granules was studied.
研究渗流铸造泡沫铝合金的性能特点,自行设计测试方法和制造测试装置,测试了泡沫铝合金的力学性能、流体透过性能、声学性能、热传导性能和阻尼性能。
5) foamed Al alloy
泡沫铝合金
1.
Performance of hollow cylindrical sandwich with high speicific strength foamed Al alloy core;
高比强泡沫铝合金中空层合圆管的性能
2.
The pouring temperature of liquid metal?preheating temperature of mould and porous body?the particle diameter ,which are interdependent and interfere each other to influence the damage degree of porous body,can influence the pore structare of foamed Al alloy.
金属液的浇注温度 ,模具与多孔体的预热温度 ,粒子粒径的大小等诸因素相互依赖相互影响 ,其结果直接影响着多孔体的损坏程度 ,从而在一定程度上影响着泡沫铝合金的孔结构。
6) Al alloy foam
泡沫铝合金
1.
Thermal decomposition properties of titanium hydride and Al alloy foam with low porosity and small pore diameter;
氢化钛热分解特性与小孔径低孔隙率泡沫铝合金
2.
Sandwich beams with high porosity and specific strength Al alloy foam core;
高比强高孔隙率泡沫铝合金三明治梁
3.
As a result, the interrelation between process parameters (presetting furnace temperature and sample temperature), foaming behavior of Al alloy foams and pore structure has been obtained.
因此,本文以PCM法为基础,通过实时摄像和断面图处理相结合方法,研究了试样温度、预设炉温(升温速度)、钢管尺寸对泡沫铝硅合金发泡特性的影响;获得了工艺参数(预设炉温、试样温度)和泡沫铝合金发泡行为及孔结构的关系,成功制取了泡沫铝硅、泡沫铝铜合金;利用自制模具,直接制备出了压缩性能试样,对不同材质、不同孔隙率、不同热处理状态的泡沫铝合金的静态压缩性能进行了测试分析;这些结果为下一步大尺寸泡沫铝的研究及应用奠定了基础。
补充资料：铝-硅系铸造铝合金
分子式：
CAS号：
性质：以硅为主要合金元素的铸造铝合金。硅的添加量范围为5％～25％，并添加镁、铜等元素，形成亚共晶型、共晶型或过共晶型合金。含硅量为5％～13％的亚共晶型或共晶型合金是工业生产中应用最广泛的铸造铝合金。良好的铸造工艺性能和气密性是它们的主要特点。含硅量在13％以上的过共晶型合金具有热膨胀系数小、耐磨性好等特点。
CAS号：
性质：以硅为主要合金元素的铸造铝合金。硅的添加量范围为5％～25％，并添加镁、铜等元素，形成亚共晶型、共晶型或过共晶型合金。含硅量为5％～13％的亚共晶型或共晶型合金是工业生产中应用最广泛的铸造铝合金。良好的铸造工艺性能和气密性是它们的主要特点。含硅量在13％以上的过共晶型合金具有热膨胀系数小、耐磨性好等特点。