1) copper residue
铜渣氯浸渣
1.
The separation and enrichment of valuable elements in copper residue slag leached by chlorine in Jinchuan company were studied by the method of sodium sulfide leaching and SO_2 neutralization.
用Na2S浸出 SO2 沉淀法对金川公司铜渣氯浸渣中有价元素的分离和富集进行了研究,分析了浸出温度、Na2S浓度,Na2S与S0 的摩尔比及浸出时间对浸出过程的影响。
2) copper waste
铜渣
1.
Production practice for producing CuSO_4·5H_2O from copper waste;
利用铜渣生产CuSO_4·5H_2O的生产实践
2.
Cu(NH 3) 2]Ac solution is prepared from copper waste in H 2SO 4—Fe—(NH 4) 2CO 3—NH 3·H 2Osystem The solution can be used to wash gases in synthetic ammonia.
利用 H2 SO4-Fe-(NH4) 2 CO3-NH3· H2 O体系由铜渣制备醋酸二氨合亚铜溶液 。
3) copper slag
铜渣
1.
The initial study on using copper slag as additional material for cement production;
工业铜渣作水泥辅料的初步探索
2.
Replacing natural silicon materia with three kinds of industrial waste residue——phosphorus slag, fly ash and copper slag, produced high quality cement clinker with the waste residues and limestone in proportion in wet process kiln.
采用磷渣、粉煤灰、铜渣三种工业废渣分别代替天然硅质原料与石灰石配料,在湿法窑上进行了生产优质熟料的工业性生产实验,结果表明:(1)采用工业废渣配料对提高湿法生产料浆的流动度,降低料浆水分,改善生料易磨性和易烧性,降低烧成温度,促进C3S的形成等有极大的帮助。
3.
The copper slag of smelter was treated, that is, changed its particle shape and particle size distributi- on, to replace river sand compounding liquid concrete.
将冶炼厂的废弃铜渣经过加工处理,改变粒径形态和颗粒级配,以替代河砂配制流态混凝土,不但可以缓解混凝土细骨料资源日趋紧缺的矛盾,降低支护成本,而且可以消除铜渣堆积造成的环境危害。
4) Copper residue
铜渣
1.
Leaching of copper residue with oxygen in sulfuric acid with participation of chloride;
硫酸介质中氯化物参与下氧化浸出铜渣过程
5) immersed copper sediment
浸铜渣
1.
The causes for the extracting rate of gold and silver from immersed copper sediment influenced by cyaniding conditions are chiefly investigated,and the best cyaniding conditions to increase the extracting rate of gold and silver are proposed as well,with the purpose of providing basis for industrial extraction of gold and silver.
结果表明,浸铜渣中NaCN用量为10 kg/t,液固比为2。
6) crude copper slag
粗铜渣
1.
This article briefly introduces two-phase oxidation acid leaching treats crude copper slag and produces above second-class copper sulphate,the slag of acid leaching is reducing smelted and dore metal containing above 80% lead and antimony alloy is produced.
简述了两段氧化酸浸处理粗铜渣,生产硫酸铜,浸出渣还原熔炼生产铅—锑合金的试验研究。
参考词条
补充资料：锅榻豆腐渣
锅榻豆腐渣
原料：豆腐渣150克，鸡蛋2个，葱10克，胡萝卜10克，精盐、味精各适量，色拉油50克。
制法：
①将豆腐渣入蒸锅蒸10分钟，取出备用。
②鸡蛋打入碗中，搅打成泡，葱切细末，胡萝卜搅汁，同入碗中加豆腐渣再次搅拌备用。
③炒锅上火，注入色拉油，油热将碗中之物倒入，炸至金黄色将味精、盐和水倒入锅中，盖上盖子焖上几分钟，汁尽出锅即成。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。