1) granulated copper slag
水淬铜渣
1.
By mixing ratio test, strength test, deformation test and durability test, it is shown that the granulated copper slag may be used as fine aggregate in concrete after adding additives Bigger weight though it had, the copper slag concrete provided the same mechanical properties and durability as ordinary concret
通过配合比、强度、变形及耐久性试验表明， 掺加了掺合料（ 大理石粉和碾细铜渣） 后，水淬铜渣（ＧＣＳ） 可作为混凝土的细集料－ 除自重较大外， 所配制的混凝土（ 铜渣混凝土） 具有与普通混凝土相同的力学性能及耐久性
2) water-quenched slag
水淬渣
1.
The experimental results showed that under the conditions with the ratio of the water-quenched slag and rectorite of 1∶1,the amount of the additive(IS) of 10%,the amount of 50% water,and the roasting temperature of 400 ℃,the spallation loss ratio of granulated composite material prepared was 0.
结果表明:水淬渣与累托石的比例为1∶1,另加入10%的添加剂(IS)和50%的水,焙烧温度为400℃,制成的复合颗粒材料的散失率为0。
2.
Factors affecting flotation of water-quenched slag from a copper smelting plant in Hubei province,such as grinding fineness,pulp density,pH value and the reagent system,were studied.
对湖北某铜冶炼厂的炼铜水淬渣(含铜1。
3.
The optimum conditions for flotation of the water-quenched slag are as follows: natural pH,Na2S 800 g/t,mixed collecting agent 240 g/t,flotation time 6 min,percent of 74 μm particles 95% and solid content 30%.
在铜熔炼反射炉渣中铜铁赋存状态分析基础上,采用常规选矿和火法贫化工艺对反射炉水淬渣进行回收铜技术探索。
3) melting slag water quenching
熔渣水淬
4) slag quenching
钢渣水淬
1.
The measures of steel-making with less-slag, BOF gas recycle, slag quenching and slab hot charge are carried out in the No.
济钢第一炼钢厂通过采取少渣炼钢、煤气回收、钢渣水淬、铸坯热送等措施,达到了充分回收和利用能源、合理使用资源、降低系统能耗、减少污染物排放、实现节能、清洁生产的目的,吨钢钢铁料消耗、炼钢工序能耗、耐材消耗分别降至1082kg、1045524。
5) water quenching slag
水淬矿渣
1.
Research on super-fine powder in water quenching slag for cement production;
水淬矿渣微细粉配制水泥的研究
6) Water Hardening Coal Dust
水淬煤渣
补充资料：铍铜熔炼过程中的搅拌除渣工业机器人(水口山矿务局)
铍铜熔炼过程中的搅拌除渣工业机器人(水口山矿务局)
铍铜熔炼过程中的搅拌除渣工业机器人 (水口山矿务局)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条