1) Craze and Transfiguration
开裂变形
1.
Analysis of Craze and Transfiguration of the Workpiece Under Wire-cutting and Pr eventive Measures;
线切割时工件的开裂变形分析及预防措施
2.
The analysis on craze and transfiguration of the cutting workpiece and preventive measures;
工件线切割时的开裂变形分析及预防措施
2) distortion and cracking
变形开裂
1.
The improved measurements are proposed,Especially the results are significant to prevent mold from distortion and cracking by adding tempering after WEDM.
结果发现:模块硬度过高、碳化物粗大、热处理工艺不当是造成模块线切割过程中开裂的主要原因,进而提出了一系列改进措施,特别是线切割后的补充回火对防止模具变形开裂效果显著。
3) Deformation and crack
变形与开裂
4) Deforming-cracking mechanism
开裂变形机制
5) cracking and deforming mechanism
开裂变形力学机制
6) m echanism ofcrack and deformation
地基开裂变形机理