2) rosin modified phenol-aldehyde epoxy resin
松香改性酚醛环氧树脂
1.
The curing process of rosin modified phenol-aldehyde epoxy resin (RPAE for short), which was self-made, with 4,4\'-diaminodiphenylsulfone, phthalic anhydride and polyamide as curing agents were traced by using FT-IR.
以自制的松香改性酚醛环氧树脂(RPAE)为对象,采用FT-IR跟踪了RPAE与三种固化剂4,4-二氨基二苯砜、邻苯二甲酸酐和聚酰胺的固化过程,得到了较佳的固化工艺,并在最佳工艺条件下对RPAE与三种固化剂组成的固化体系进行固化,并用FT-IR、TG等表征手段考察了固化物的结构和性能。
2.
Kinetics of curing reaction of rosin modified phenol-aldehyde epoxy resins(RPAE) with 4,4\'-diamino diphenyl sulphone(DDS) was investigated by DSC.
以自制的松香改性酚醛环氧树脂(RPAE)为对象,采用差示扫描量热法研究了其与4,4-二氨基二苯砜组成的体系(RPAE/DDS)的固化动力学,利用Kissinger方程计算得到体系的固化热约为109。
4) HF-Ⅰ modified epoxy-resin
HF-Ⅰ环氧改性酚醛树脂
5) silicone modified phenolic epoxy resin
有机硅改性酚醛环氧树脂
1.
A silicone modified phenolic epoxy resin(SMPER) as sand control agent(SCA) is developed to solve severe sanding problems in oil wells in fine siltstone reservoirs of Shengli.
针对胜利油田出砂严重的细粉砂岩油藏的油井,研制了有机硅改性酚醛环氧树脂稳砂剂。
6) novolac-epoxy resin
热塑性酚醛型环氧树脂
补充资料：酚醛环氧树脂
分子式：
CAS号：
性质：是由苯酚或邻甲酚与甲醛反应制得的酚醛树脂，再与环氧氯丙烷反应而成的一类树脂。其特点是每分子的环氧官能度都大于2，可使涂料的交联密度大，耐热性和耐化学品性高于双酚A型环氧树脂，但漆膜较脆，附着力稍低，一般需较高的固化温度，故常与双酚A环氧树脂合用，或用双酚A环氧树脂作底漆，用酚醛环氧树脂作中涂层及面漆。
CAS号：
性质：是由苯酚或邻甲酚与甲醛反应制得的酚醛树脂，再与环氧氯丙烷反应而成的一类树脂。其特点是每分子的环氧官能度都大于2，可使涂料的交联密度大，耐热性和耐化学品性高于双酚A型环氧树脂，但漆膜较脆，附着力稍低，一般需较高的固化温度，故常与双酚A环氧树脂合用，或用双酚A环氧树脂作底漆，用酚醛环氧树脂作中涂层及面漆。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条