1) epoxy-phenolic(ZnO) resin
环氧-酚醛(锌)树脂
2) Phenolic epoxy resin
酚醛环氧树脂
1.
Preparation of water-borne phenolic epoxy resin latex;
水性酚醛环氧树脂乳液的制备
2.
Preparation of phenolic epoxy resin high-temperature resistance adhesives modified with silicone;
有机硅改性酚醛环氧树脂耐高温胶粘剂的研制
3.
In this essay,the chain transfer agent RAFT made in our laboratory has a reaction with phenolic epoxy resin.
本文采用本实验室制备的一种RAFT链转移剂,先与酚醛环氧树脂进行加成反应,然后通过控制丙烯酸的量再对加成后树脂进行改性,制备出了水溶性酚醛树脂;采用FTIR、GPC、DSC等测试手段对树脂的结构进行了表征,并对其性能进行了研究。
3) novolac epoxy
酚醛型环氧树脂
1.
Study on curing kinetics of novolac epoxy/bisphenol A cyanate resin system;
酚醛型环氧树脂/双酚A型氰酸酯树脂体系固化动力学的研究
4) Novolac Epoxy Resin
酚醛环氧树脂
1.
Allyl group was grafted into novolac epoxy resin,in order to take on photosensitivity.
通过在酚醛环氧树脂中引入烯丙基,以实现树脂的感光性,考察了四种催化剂和其不同用量及两种阻聚剂对反应的影响,利用配比不同的丙烯酸和酚醛环氧树脂合成出的感光预聚物,研究了其对感光组合物性能的影响。
2.
Two kinds of cyanate - epoxy resin blends, bisphenol A dicyanate - bisphenol A diglycidyl ether epoxy resin blends and bisphenol A dicyanate - novolac epoxy resin blends were prepared via melt blending process.
通过熔融共混制备了双酚A二氰酸酯/双酚A二缩水甘油醚环氧树脂、双酚A二氰酸酯/酚醛环氧树脂两种共混物。
3.
By mixing epoxy resin E-51 and novolac epoxy resin F-51 with weight ratio 1:1 the mix resin was compounded.
环氧树脂E-51和酚醛环氧树脂F-51以质量比1:1配制成混合树脂,以占环氧树脂15%的CTBN为增韧改性剂,制成预聚物,再与改性芳香胺固化剂、邻甲酚缩水甘油醚、耐高温填料等配合,配制成HT-737耐高温胶粘剂,满足了某军用飞机天线中聚苯硫醚与镀银黄铜板的粘接密封。
5) epoxy-phenolic resin
酚醛环氧树脂
1.
A special waterborne photosensitive epoxy-phenolic resin was synthesized by modification of F-44 epoxyphenolic resin with acrylic acid and succinic anhydride.
用丙烯酸和琥珀酸酐对F-44酚醛环氧树脂进行改性,合成了一种水性光敏酚醛环氧树脂。
2.
A water soluble photosensitive epoxy-phenolic resin was synthesized by modifying acrylic F-44 epoxy-phenolic resin with succinic anhydride.
用琥珀酸酐对丙烯酸改性的F-44酚醛环氧树脂作进一步的改性,合成了一种具有光敏性的水性酚醛环氧树脂,研究了催化剂种类、反应温度及反应时间对琥珀酸酐转化率的影响,并考察了原料配比对改性树脂水溶性、力学性能和耐腐蚀性能的影响。
6) epoxy phenolics
环氧酚醛树脂
1.
A phosphate flame retardant containing halogen(tris-2-chloroethyl phosphate) and inorganic flame retardant(aluminum hydroxide) were introduced into neat epoxy phenolics and paper-sludge/ epoxy-phenolic composite in order to improve their flame retardancy.
将含各类阻燃剂加入到环氧酚醛树脂和纸泥/环氧酚醛聚合物中,用UL-94等级燃烧测试法测定体系的燃烧等级,结果表明:TCEP和无机阻燃剂对环氧酚醛树脂有阻燃作用,但卤化和磷酸化的阻燃剂能增强纸浆/环氧酚醛复合材料的阻燃性。
2.
A phosphate flame retardant containing halogen(tris-2-chloroethyl phosphate) and inorganic flame retardant(aluminum hydroxide) were introduced into neat epoxy phenolics and paper-sludge/epoxy-phenolic composite in order to improve their flame retardancy.
用热塑性环氧酚醛树脂与纸泥制备纸泥/环氧酚醛复合材料,将含卤素的阻燃剂三-2-氯乙基膦酸盐和无机阻燃剂(如氢氧化铝)加入到环氧酚醛树脂和纸泥/环氧酚醛聚合物中,用UL-94等级燃烧测试法测定体系的燃烧等级;用热重分析仪和差示扫描量热仪对复合材料进行热分析,研究两体系的阻燃性。
补充资料：线型酚醛环氧树脂
分子式：
CAS号：
性质：学名线型酚醛多缩水甘油醚。俗名F型环氧树脂。含线型酚醛树脂结构的多缩水甘油醚。环氧官能度2.2～5.5，随分子量不同呈黏稠状液体至固体。环氧当量172～200g/eq。固化物交联密度大，机械性能和耐热性能好。热变形温度177℃，较双酚A型高20℃。其玻璃布层合板弯曲强度377MPa；体积电阻率5.2×1015Ω·cm。由苯酚与甲醛制得的聚合度3～5的线型酚醛树脂，再与环氧氯丙烷反应而成。主要用作电器用层合材料、结构件、耐热黏合剂和涂料、包封及灌封料。特别是缠绕成型作化工用管、泵体和贮槽等。
CAS号：
性质：学名线型酚醛多缩水甘油醚。俗名F型环氧树脂。含线型酚醛树脂结构的多缩水甘油醚。环氧官能度2.2～5.5，随分子量不同呈黏稠状液体至固体。环氧当量172～200g/eq。固化物交联密度大，机械性能和耐热性能好。热变形温度177℃，较双酚A型高20℃。其玻璃布层合板弯曲强度377MPa；体积电阻率5.2×1015Ω·cm。由苯酚与甲醛制得的聚合度3～5的线型酚醛树脂，再与环氧氯丙烷反应而成。主要用作电器用层合材料、结构件、耐热黏合剂和涂料、包封及灌封料。特别是缠绕成型作化工用管、泵体和贮槽等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。