1) transverse corner crack
角横裂
1.
This article brings forward the reasons and countermeasures of the transverse corner crack and surface longitudinal crack of the CC slab.
简述了太钢二炼钢厂碳钢连铸生产线生产的板坯出现的缺陷,分析了板坯的角横裂、表面纵裂的成因,提出了防止裂纹而采取的措施。
2.
Longitudinal and transverse corner crack defects were found on the slab surface for peritectic steel grade Q235G cast in Panzhihua Iron and Steel Group Company.
针对攀钢连铸 Q2 35 G等包晶钢生产中出现的铸坯表面裂纹问题 ,在调查分析裂纹特征及其产生原因的基础上 ,发现保护渣传热过强和保护渣流入不均是诱发角横裂产生的主要原因。
3.
The possibility of transverse corner cracking in slab of peritectic carbon steel is greater than that of other carbon steels.
介绍了影响包晶碳钢角横裂的连铸工艺操作和设备。
2) transverse corner crack
角部横裂
1.
Causes and countermeasures of transverse corner crack on narrow continuous casting slab;
连铸窄板坯角部横裂的成因及对策
3) transverse corner cracks
角部横裂纹
1.
Factors influencing transverse corner cracks in continuous casting slab,such as level fluctuation of molten steel in mold,mold taper,primary cooling,casting powder,secondary cooling,process parameters of CC,etc.
分析了结晶器液面波动、结晶器锥度、结晶器冷却制度、连铸保护渣、二冷制度等连铸工艺对低合金钢板坯角部横裂纹缺陷的影响,在此基础上,提出了改善板坯角部横裂纹的有效措施,即稳定结晶器液面、优化结晶器锥度、弱化结晶器冷却和连铸二次冷却,改进连铸保护渣等。
5) corner and transverse crack
表面角部横裂纹
1.
This paper analyzes reasons to form corner and transverse crack on the surface of 150?mm CC billet based on Anyang Steel's production practice.
结合安钢150mm连铸小方坯表面角部横裂纹攻关的实践分析其成因,提出了改进措施,实施后取得了良好的效果。
6) transverse crack
横裂
1.
The reason for transverse crack in continuous-casting slab is analyzed,some treasures proposed.
分析了临钢板坯连铸机板坯产生横裂纹的原因,找出了消除板坯产生横裂的处理措施。
2.
Through an analysis of the material, microstructure, spheroidization mechanizm and the process of spheroidizing techniqe,a conclusion can be drawn that non uniform furnace temperature and lower local heating temperature lead to the abnormal structure speroidization underheated structure,which in turn results in transverse crack under the complex stresses in cold drawing.
通过材质分析、金相组织分析、球化机理的探讨及对球化工艺过程的追溯 ,得出GCr15轴承钢管冷拔产生横裂的主要原因是由于炉温不均、局部加热温度偏低而产生的球化退火欠热型反常组织在冷拔过程的复杂应力作用下产生裂纹所致。
3.
Because Nb is a crack-sensitive element, the transverse cracking rate of the Nb containing slab is far greater than that of other steel grade.
为降低生产成本,济钢第一炼钢厂方坯铸机以铌铁代替钒铁生产HRB400等含铌钢种,由于铌为裂纹敏感性元素,其铸坯横裂纹发生率远远大于其它钢种。
补充资料：横裂
transversecrack：垂直于炭化室内热流方向的焦炭裂纹。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。