1) sulphurized oxymolybdenum dialkyldithiophosphate
二烷基二硫代磷酸硫化氧钼
1.
It is synthesized sulphurized oxymolybdenum dialkyldithiophosphate under catalyst of HY1 acidic cation-exchange resin,the reaction time is 6h,the amount of catalyst is 12%,and the yield rate of sulphurized oxymolybdenum dialkyldithiophosphate comes to 85%.
用HY1酸性阳离子交换树脂催化剂,合成了二烷基二硫代磷酸硫化氧钼,反应时间为6h,催化剂的质量分数为12%,二烷基二硫代磷酸硫化氧钼的收率为85%。
2) Oxymolybdenum dialkydithiophosphate
二烷基二硫代磷酸氧钼
3) dialkyl sulfurized oxymolybdenum organophosphorodi thicate
二烷基二硫代磷酸硫化氧钼盐
4) molybdenum dialkyldithiophosphate
二烷基二硫代磷酸钼
1.
A four-ball machine was used to evaluate the extreme pressure and antiwear (EP&AW) properties of molybdenum dialkyldithiophosphate (MoDDP) in 150N paraffinic base oil and two formulated oils, SJ15W/40 and SH15W/40, and its antiwear synergistic effect with zinc dialkyldithiophosphate (ZnDDP) was investigated.
采用四球试验机评价二烷基二硫代磷酸钼(MoDDP)化合物在150SN石蜡基基础油和SJ 15W／40、SH 15W／40成品油中的极压抗磨性能,考察MoDDP与二烷基二硫代磷酸锌(ZnDDP)的抗磨协同效应,并分析了抗磨作用机理。
5) Sulfurized oxymolybdenum di-(2-ethylhexyl)phosphorodithioate
硫化二(2-乙基已基)二硫代磷酸氧钼
6) -thioxodi-Molybdenum
二(2-乙基己基)二硫代磷酸氧硫化钼
补充资料：二硫化钽
分子式：TaS2
CAS号：
性质：黑色粉末。有两种晶型：六方晶(晶格常数a=0.3315nm)和斜方六面体结构(晶格常数a=0.332nm)。有良好的热化学稳定性，空气中300℃才开始氧化。在水中稳定，但易为浓硫酸、硝酸、过氧化氢溶液、碱液所分解。在600～800℃下使钽粉和硫蒸气反应生成，或在800～1000℃时由五氧化二钽和硫化氢反应制取。有良好的导电性和较低的摩擦系数，用作固体润滑剂。