1) NZP family porous ceramics
NZP族多孔陶瓷
1.
The NZP family porous ceramics with different chemical composition were obtained byadding pore-forming agent, dry pressing molding and sintering in 1100℃.
以不同化学组成的NZP族磷酸盐粉体为陶瓷骨料,采用添加造孔剂的方法,经干压成型,1100℃烧结制备出NZP族多孔陶瓷。
2) NZP family ceramics
NZP族陶瓷
3) phosphate cramic material in NZP family
NZP族磷酸盐陶瓷
4) NZP family ceramics
NZP陶瓷
1.
4Zr4(PO4),(CM), which is a low thermal conductivity and excellent thermal shock resistance ofcompositinn in NZP family ceramics, are synthesized by coprecipitation method.
NZP陶瓷具有低膨胀、低导热、高抗热震性，是用于隔热抗热震场合的理想材料，本文采用沉淀法合成CM粉料、等静压成型、分段烧成制度，成功地制备出NZP陶瓷增压器蜗壳隔热管。
5) porous ceramic
多孔陶瓷
1.
Fabrication of Porous Ceramic With Starch as the Pore-forming Agent;
以淀粉作造孔剂制备多孔陶瓷
2.
Preparation of TiO_2 porous ceramic;
TiO_2多孔陶瓷的制备
3.
Al_2O_3 matrix porous ceramics prepared by SHS;
燃烧合成法制备的Al_2O_3基多孔陶瓷
6) porous ceramics
多孔陶瓷
1.
Preparation and development of porous ceramics;
多孔陶瓷制备技术的进展
2.
Fabrication of porous ceramics using polymeric sponge dipping method;
有机泡沫浸渍法制备多孔陶瓷
3.
Research on fabrication of warp-knitted space porous ceramics by impregnation process;
由浸渍工艺制备经编间隔结构多孔陶瓷的研究
补充资料：多孔陶瓷
分子式：
CAS号：
性质：含有大量气孔的陶瓷制品。具有较高的机械强度、良好的化学稳定性和耐温度急变性。以黏土、长石、石英等为原料，并加发泡剂，有时也加入一些可燃烧的有机物，在坯体烧成过程中生成大量气孔。成型采用注浆、热压铸、捣打、等静压、挤管等方法。按气孔形式可分为闭口气孔和贯通性开口气孔两类。孔径范围一般为0.1～300μm，也有在0.1μm以下的(如用作过滤器)。闭口气孔陶瓷多用作空心球、绝热或隔音材料。孔径分布均匀的贯通性开口气孔陶瓷多用作催化剂载体(坯料)、沸腾床气体分布板、固液、固气分离用过滤器，以及制作无机分离膜的支撑体(无机分离膜用溶胶-凝胶法制造，用于制作新型过滤器)等。
CAS号：
性质：含有大量气孔的陶瓷制品。具有较高的机械强度、良好的化学稳定性和耐温度急变性。以黏土、长石、石英等为原料，并加发泡剂，有时也加入一些可燃烧的有机物，在坯体烧成过程中生成大量气孔。成型采用注浆、热压铸、捣打、等静压、挤管等方法。按气孔形式可分为闭口气孔和贯通性开口气孔两类。孔径范围一般为0.1～300μm，也有在0.1μm以下的(如用作过滤器)。闭口气孔陶瓷多用作空心球、绝热或隔音材料。孔径分布均匀的贯通性开口气孔陶瓷多用作催化剂载体(坯料)、沸腾床气体分布板、固液、固气分离用过滤器，以及制作无机分离膜的支撑体(无机分离膜用溶胶-凝胶法制造，用于制作新型过滤器)等。