1) porous SiC ceramics
多孔SiC陶瓷
1.
Two kinds of methods were used to prepare porous SiC ceramics (PSC).
采用两种不同的方法制备多孔SiC陶瓷 ,讨论了其显微组织对性能的影响 ,探索了由天然木材经炭化、渗硅处理制造多孔SiC陶瓷的新方法 。
2.
The quasi-static compressive properties and the fracture morphology of 4 kinds of porous SiC ceramics/Zr-base amorphous alloy composites were investigated with the WDW-E100D testing machine and the S-4800 scanning electronic microscope(SEM).
利用WDW-E100D型万能试验机和S-4800场发射扫描电镜,研究了不同工艺制备的多孔SiC陶瓷/Zr基非晶合金复合材料的准静态压缩性能和断口形貌特征。
2) porous SiC ceramics
SiC多孔陶瓷
1.
The porous SiC ceramics were prepared by vacuum sintering in this investigation,the effect of different sintering aids,Al2O3-Y2O3 and Si,and different pore formers,acrylamide copolymer and Carboxymethyl Cellulose(CMC) on the microstructures and porosity were studied.
采用真空烧结方法制备了SiC多孔陶瓷,研究了不同助烧结剂Al2O3-Y2O3、Si以及不同造孔剂丙烯酰胺聚合物、羧甲基纤维素(CMC)对SiC多孔陶瓷形貌和气孔率的影响。
2.
Properties of the two kinds of porous SiC ceramics using PCS and SR as binder respectively were analyzed and compared.
分别以聚碳硅烷和硅树脂作粘结剂,SiC微粉作骨料,在惰性气氛中1000℃下低温制备出SiC多孔陶瓷,所得样品的气孔率在43%~52%之间,抗断裂强度最高达到了18。
3.
The flexural strength of porous SiC ceramics increased with increasing PCS content and shaping pressure,while decreased with increasing the carbon content.
以聚碳硅烷为粘接剂,SiC粉末为骨料,经模压成型、惰性气氛保护下于1000℃裂解低温制得SiC多孔陶瓷。
3) SiC porous ceramics
SiC多孔陶瓷
1.
The SiC porous ceramics preforms were fabricated by vacuum sintering, and the effects of different sintering aids including Al2O3-Y2O3, Si, Co and Kaolin as well as the content of Carboxymethyl Cellulose (CMC) on the porosity and microstructure of the SiC porous ceramics preforms were studied.
本文采用真空烧结方法制备SiC多孔陶瓷预成形坯,研究了不同助烧结剂Al2O3-Y2O3、Si、Co和高岭土以及造孔剂羧甲基纤维素(CMC)含量对SiC多孔陶瓷预成形坯气孔率和形貌的影响。
2.
Bio-morphology SiC porous ceramics was fabricated by the reaction infiltration of SiO vapor with the carbonized bamboo.
以毛竹为原材料,碳化后制得竹炭为模板,采用气相SiO反应渗透法制备了生物形态SiC多孔陶瓷。
4) porous silicon carbide based ceramics
多孔SiC基陶瓷
6) Ordered-porous SiC(Fe) ceramic
有序多孔SiC(Fe)陶瓷
补充资料:多孔磷酸钙生物陶瓷
分子式:
CAS号:
性质: 是一种含活体细胞的骨替换材料。生物陶瓷为其提供良好的生物相容性和骨传导性;骨髓细胞作为其成骨细胞的源,赋予材料骨诱导性。可用于长骨段缺损的修复。
CAS号:
性质: 是一种含活体细胞的骨替换材料。生物陶瓷为其提供良好的生物相容性和骨传导性;骨髓细胞作为其成骨细胞的源,赋予材料骨诱导性。可用于长骨段缺损的修复。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条