1) surface in-situ chemistry multi-modification
表面原位化学组合改性
2) in situ combined chemical modification
原位组合化学改性
3) Electrochemical surface modification
电化学表面改性
4) surface modification
表面化学改性
1.
The optimum process conditions of surface modification of wollastonite were suggested as follows: modification reagent stearic acid,modification reagent dosage 2%,modification time 15～20 min,modification temperature 70 ℃.
通过对超细硅灰石粉体的表面化学改性效果的研究,确定了最佳工艺条件:改性剂为硬脂酸,改性剂用量2%,改性时间15~20min,改性温度70℃。
6) Surface Chemical Modification
表面化学改性
1.
The surface chemical modification of ultrafine sericite was carried out by using silane coupling agent.
采用硅烷偶联剂对超细绢云母进行表面化学改性 ,通过对径厚比、改性绢云母填充量等变量的研究 ,探讨改性绢云母增强尼龙 6力学性能的变化规律 。
2.
With natural minerals as raw materials, silicone rubber reinforcement fillers, namely the modified ultrafine powders with excellent properties, are prepared through ultrafine crashing, surface chemical modification and mechanical chemical modification.
以天然矿物滑石、石英、粒状硅灰石和针状硅灰石为原料，经超细粉碎、表面化学改性和机械力化学改性等三种工艺方法进行深加工，制备出具有优良性能的超细粉体材料———硅橡胶增强填料，其性能接近气相白碳黑，可部分代替白碳黑用于硅橡胶。
3.
With ultrafine crashing and surface chemical modification, hard|sericite was modified.
采用超细粉碎和表面化学改性方法对硬质绢云母进行改性 ,研究表面改性的机理 ,建立了一整套的改性工艺 ,制备出应用性能和价值得到较大提高的改性硬质绢云母超细粉。
补充资料：表面改性剂
分子式：
CAS号：
性质：有机颜料在表面处理过程中，为使其粒子表面极性与所使用的分散介质(如连接料或展色料、有机溶剂)具有良好的相容性或匹配性，需在添加表面处理剂或包覆剂时，常常首先添加具有特定取代基(如磺酸基、氨基等)的表面改性剂，吸附在粒子表面上，然后添加表面处理剂，使其与表面改性剂以化学键、离子对或氢键等方式结合，最后使表面处理剂更牢固地吸附于颜料表面，达到颜料粒子的改性目的。
CAS号：
性质：有机颜料在表面处理过程中，为使其粒子表面极性与所使用的分散介质(如连接料或展色料、有机溶剂)具有良好的相容性或匹配性，需在添加表面处理剂或包覆剂时，常常首先添加具有特定取代基(如磺酸基、氨基等)的表面改性剂，吸附在粒子表面上，然后添加表面处理剂，使其与表面改性剂以化学键、离子对或氢键等方式结合，最后使表面处理剂更牢固地吸附于颜料表面，达到颜料粒子的改性目的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条