1) point seed
点状籽晶
1.
DKDP crystals were grown by the Z cut point seed (5mm×5mm×3mm) on the basis of the study on the stability of DKDP solution.
本文在研究DKDP溶液稳定性的基础上 ,采用Z切点状籽晶 (5mm× 5mm× 3mm)生长了多块DKDP晶体 ,在2 5 0ml和 10 0 0ml生长瓶中分别获得了在 [10 0 ]和 [0 0 1]向生长速度可达到 3mm/d和 4 5mm/d的点状籽晶生长优质DKDP晶体的生长条件。
2) "point-seed" method
"点籽晶"法
3) seed
[英][si:d] [美][sid]
籽晶
1.
Study on the growth habit and optical property of DKDP crystal grown by different seed
不同籽晶DKDP晶体生长和光学性能研究
2.
Microstructural evolution during directional solidification(DS)of Ti-47Al alloy grown from Ti-43Al-3Si seed was studied.
以Ti-43Al-3Si为籽晶,对Ti-47Al合金籽晶法定向凝固过程中的相选择和组织演化规律进行了研究。
3.
The evolution of solid/liquid interface during single crystal superalloy growth by seeding technique was investigated.
研究了籽晶法生长单晶高温合金中固液界面的演变规律。
4) seeds
籽晶
1.
AlOOH nanometer powders were prepared from Al(NO_3)_3·9H_2O and ammonia by adding seeds through hydrothermal method.
利用SEM和粒度仪分析了不同水热温度以及不同籽晶对晶粒形貌的影响。
2.
The effect of α-Al2O3 seeds (-150nm) on the phase transformation and micrograph of alumina was studied.
在湿化学法合成的纳米Al2O3前驱体NH4Al(OH)2CO3中添加α-Al2O3籽晶(150nm左右),研究了α-Al2O3籽晶对Al2O3晶型转变及形貌的影响。
3.
In the present dissertation,the study is on fabricating high quality hydrothermal ZnO crystals,is on influences on crystal s appearances and quality under growing conditions of spontaneous crystallizations,is on manufacturing autoclave with lining for growing large size ZnO crystals,is on crystal s quality under varied growing conditions with seeds.
本文研究水热自发结晶的生长条件对ZnO晶体形貌和质量的影响,研制用于生长较大尺寸晶体的防腐高压釜,研究水热有籽晶生长的条件对ZnO晶体质量的影响,比较两者的生长习性和生长机理,结合ZnO晶体-c面和+c面退火前后性能的研究,探索晶体中的缺陷变化对其光电性能的影响。
5) Seeding
[英][si:d] [美][sid]
籽晶
1.
TiAl Seed Preparation & Fully Lamellar Structure Control Through Seeding and Directional Solidification;
TiAl籽晶制备及定向全片层组织的研究
2.
Milling process, α-Al_2O_3 seeding, and some additives such as TiO_2, MgO, NH_4NO_3, etc, were usually adopted to decrease the α-phase transformation temperature, leading to producing ultrafined and agglomeration-free alumina powder.
通过对氧化铝前驱体的球磨 ,在前驱体中引入α氧化铝籽晶 ,或者加入TiO2 ,MgO ,NH4 NO3等矿化剂可以降低氧化铝前驱体的α相变温度 ,从而得到粒径细小、无硬团聚的氧化铝粉体。
3.
Then, we utilized the additives of α -AL_2O_3 powder seeding, alumina sol seeding, TiO_2-sol , ammonium nitrate , and high-energy ball milling on the precursors to investigate these factors'.
接着，就分别研究在前驱体中加入或掺杂Q-Al_2O_3粉体籽晶、氧化铝胶体籽晶、TiO_2溶胶、硝酸铵以及高能球磨前驱体等一系列因素对α相变温度、最终产物微结构、相变过程等的影响。
6) seed crystal
籽晶
1.
Natural diamond with seed crystal is discovered for the first time in Hunan Province by the study of synchrotron radiation X-ray diffraction topography.
利用同步辐射X射线形貌学研究,首次发现湖南褐色天然金刚石中存在籽晶金刚石。
补充资料：铝合金的羽毛状晶
铝合金的羽毛状晶
feathey crystal of aluminium alloy
IUheJ旧deyumooZhuangJ旧g铝合金的羽毛状晶(feathey Crystal of alu-minium anoy)铝合金铸锭中柱状晶的变种，形状类似羽毛的晶粒。是铸锭缺陷的一种。形状近似直线状花边的羽毛状晶亦称为“花边状组织”。羽毛状晶成群出现，每群中羽毛状晶之间近似平行。羽毛状晶是双晶，以(111)晶面为双晶面。铝一镁系合金中的羽毛状晶如图所示。’ 产生羽毛状晶的工艺因素主要是:(1)熔体处于高温平稳状态，有较好的定向结晶条件。(2)在铸造温度下熔体停留时间过长，熔体过热和高度净化，减少结晶前沿形成晶核的数量。(3)合金中加入某些容易产生羽毛状晶的微量元素，如硼和错。 超硬铝合金、工业纯铝和高镁铝合金形成羽毛状晶的几率较大，而高强锻造铝合金2A70(LD7)、防锈铝合金 3A21(LF21)和含镁低于5%的铝镁系合金，基本上不形成羽毛状晶。 铸锭中存在羽毛状晶对其性能影响较大。在塑性加工过程中易在羽毛状晶的双晶面处产生裂纹。制品中残留的未完全破碎的羽毛状晶区会扩大使用性能的各向异性。蘸: 铝一镁系合金铸锭中的羽毛状晶偏光只100 (格长清)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条