1) PREP
[英][prep] [美][prɛp]
等离子旋转电极工艺
1.
The high nitrogen steels (HNS) were produced by plasma rotating electrode process (PREP), and the properties of HNS specimens were examined.
为了寻求高效、经济的高氮钢生产工艺,用等离子旋转电极工艺(PREP)生产高氮钢并测试了所生产的几种典型高氮钢的性能。
2.
The spherical Ni based superalloy powder is used for X ray interior cleanness inspection and shot peening of turbine blades The production of this powder by Plasma Rotating Electrode Process(PREP)has been Studied.
本文对采用等离子旋转电极工艺 (PREP)生产该种类型粉末进行了研究 ,探讨了棒料转速、等离子电流强度等对粉末收得率的影响 ,获得了最佳的生产工艺参数。
3.
Effect of PREP Process Parameters on Powder Properties for FGH95 Superalloy;
研究了采用等离子旋转电极工艺制取FGH95高温合金粉末时各主要工艺参数对粉末平均粒度及其分布的影响。
2) plasma-rotating electrode
等离子旋转电极
3) PREP
[英][prep] [美][prɛp]
等离子旋转电极雾化
1.
Pre-heat treatment of PREP FGH95 superalloy powders;
等离子旋转电极雾化FGH95高温合金粉末的预热处理
4) plasma-rotating electrode process
等离子体旋转自耗电极
5) plasma rotating electrode process
等离子旋转电极法
6) PlasmaKinetic electrode
等离子电极
1.
Methods:We performed transurethral urethroplasty for 11 patients with urethratresia using the PlasmaKinetic electrodes under the guidance of C arm xanthippe.
方法:在C型臂X光机引导下,对11例尿道闭锁患者行等离子电极尿道腔内成形术。
补充资料：旋转电极制粉法
旋转电极制粉法
rotating electrode comminuting process
xuanZhuand旧nji zhifenf。 旋转电极制粉法(护tating electrodeco， minutingProc郎的以金属或合金制成自耗电 极，其端面受电弧加热而熔融为液体，通过电极高速旋 转的离心力将液体抛出并粉碎为细小液滴，继之冷凝 为粉末的制粉方法。这种制粉方法子1974年首先由 美国核金属公司开发成功，其工作原理示于图。它在熔 融和雾化金属过程中完全避免了造渣和与耐火材料接 慈消除了非金属夹杂物污染源，可生产高洁净度的粉 末·_- -一_瞬_ 1一电弧;2一粉末:3一旋转自能金属或合金电极。4一固定钨电极 典型的旋转电极制粉设备是由一个直径达Zm多 的箱体组成，旋转自耗电极通过动密封轴承装入其中， 电极长轴水平地处于箱体中心线位置，电极旋转速度 高达1 5000~25。。0r/mino一为了避免钨污染，可在钨电 极处改用等离子炬，称为等离子旋转电极雾化制粉法 (P REP)放用电子束熔融自耗电极，称为电子束旋转 盘雾化制粉法(E BRD)。箱体内的保护气氛可选用惰 性气体，最好是氢气。因为它的热导率最高，几乎是氢 气咖磅沱既能提高冷却速瓦又可改善瓤眺。 旋转电极法制取的粉末，其粒度分布范围比较窄 (50一50如m)，平均粒度可近似地认为与自耗电极旋〕疑潺{翼l辨瀚 流 理 夕右 钦 合金(Ti‘。Ai一4v)和镍基高温合金(例如美国牌号 IN10。和Rene，5)已成功地用于制造航空燃气涡轮发 动机压气机转子和涡轮盘等零部件。 ‘(再洪海)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。